A Novel Technique for Growing Crack-Free GaN Thick Film by Hydride Vapor Phase Epitaxy

Abstract

To prevent the cracking of GaN thick films grown on a sapphire substrate by hydride vapor phase epitaxy (HVPE), a novel technique without complex processes is developed. By adding a temperature ramping step in the HVPE GaN epitaxy process, more than 300-mu m-thick high-quality crack-free GaN thick films on sapphire substrate can be obtained by this technique. After separation by a conventional laser-induced lift-off process, a 1.5 in. 300 mu m freestanding GaN wafer with a dislocation density of approximately 1 x 10(7) cm(-2) could be fabricated without any cracks. No additional designed-patterned or stress-reduced structures were applied in these samples to reduce the dislocation density and thermal stress. [DOI: 10.1143/JJAP.47.8394]