dc.description.abstractThe effects of Mg microadditions on the high-temperature/low stress (1255 K/200 MPa) creep properties and fracture behavior of a Mar-M247 superalloy were investigated in this study. The results of quantitative statistical analyses showed that when Mg microadditions up to 50 ppm were made, the MC carbides located at grain boundaries (designated GB MC) were significantly refined and spheroidized and the number of MC carbides decreased. In addition, the M23C6 carbides present on GBs dramatically increased with increasing Mg contents up to 50 ppm, and the creep resistance was enhanced under the test condition of 1255 K/200 MPa. However, the creep performance of a Mar-M247 superalloy containing 80 ppm Mg deteriorated due to the formation of an extremely large amount of MC carbide and a decrease in the number of M23C6 carbides at GBs. The cracks mainly initiated and propagated along GBs in both the Mg-free and Mg-containing Mar-M247 superalloys under 1255 K/200 MPa, and the finial rupture was caused by intergranular fracture. Under the present creep condition, the optimal Mg microaddition to a Mar-M247 superalloy should be 30 to 50 ppm.en_US
dc.language.isoen_USen_US
dc.titleThe influence of Mg on creep properties and fracture behaviors of Mar-M247 superalloy under 1255 K/200 MPaen_US
dc.typeArticleen_US
dc.identifier.journalMETALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCEen_US
dc.citation.volume31en_US
dc.citation.issue5en_US
dc.citation.spage1365en_US
dc.citation.epage1373en_US
dc.contributor.department材料科學與工程學系zh_TW
dc.contributor.departmentDepartment of Materials Science and Engineeringen_US
dc.identifier.wosnumberWOS:000087110800005-
dc.citation.woscount5-
Appears in Collections:Articles


Files in This Item:

  1. 000087110800005.pdf

If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.