An integrated cobalt disulfide (CoS2) co-catalyst passivation layer on silicon microwires for photoelectrochemical hydrogen evolution
(2015-01-01)
Chen, Chih-Jung
;
Chen, Po-Tzu
;
Basu, Mrinmoyee
;
Yang, Kai-Chih
;
Lu, Ying-Rui
An integrated cobalt disulfide (CoS2) co-catalyst passivation layer on Si microwires (MWs) was used as a photocathode for solar hydrogen evolution. Si MWs were prepared by photolithography and dry etching techniques. The CoS2Si photocathodes were subsequently prepared by chemical deposition and thermal sulfidation of the Co(OH)(2) outer shell. The optimized onset potential and photocurrent of the CoS2Si electrode were 0.248 V and -3.22 mA cm(-2) (at 0 V), respectively. The best photocatalytic activity of the CoS2Si electrode resulted from lower charge transfer resistances among the photoabsorber, co-catalyst, and redox couples in the electrolyte. X-ray absorption near edge structure was conducted to investigate the unoccupied electronic states of the CoS2 layer. We propose that more vacancies in the S-3p unoccupied states of the CoS2Si electrode were present with a lower negative charge of S-2(2-) to form weaker S-H bond strength, promoting water splitting efficiency. Moreover, the CoS2 co-catalyst that completely covered underlying Si MWs served as a passivation layer to prevent oxidation and reduce degradation during photoelectrochemical measurements. Therefore, the optimal CoS2Si electrode maintained the photocurrent at about -3 mA cm-2 (at 0 V) for 9 h, and its hydrogen generation rate was approximately 0.833 mu mol min(-1).
Wide Range pH-Tolerable Silicon@Pyrite Cobalt Dichalcogenide Microwire Array Photoelectrodes for Solar Hydrogen Evolution
(2016-03-02)
Chen, Chihjung
;
Yang, Kai-Chih
;
Basu, Mrinmoyee
;
Lu, Tzu-Hsiang
;
Lu, Ying-Rui
This study employed silicon@cobalt dichalcogenide micro wires (MWs) as wide range pH-tolerable photocathode material for solar water splitting. Silicon microwire arrays were fabricated through lithography and dry etching technologies. Si@Co(OH)(2) MWs were utilized as precursors to synthesize Si@CoX2 (X = S or Se) photocathodes. Si@CoS2 and Si@CoSe2 MWs were subsequently prepared by thermal sulfidation and hydrothermal selenization reaction of Si@Co(OH)(2), respectively. The CoX2 outer shell served as cocatalyst to accelerate the kinetics of photogenerated electrons from the underlying Si MWs and reduce the recombination. Moreover, the CoX2 layer completely deposited on the Si surface functioned as a passivation layer by decreasing the oxide formation on Si MWs during solar hydrogen evolution. Si@CoS2 photocathode showed a photocurrent density of -3.22 mA cm(-2) at 0 V (vs RHE) in 0.5 M sulfuric acid electrolyte, and Si@CoSe2 MWs revealed moderate photocurrent density of -2.55 mA cm(-2). However, Si@CoSe2 presented high charge transfer efficiency in neutral and alkaline electrolytes. Continuous chronoamperometry in acid, neutral, and alkaline solutions was conducted at 0 V (vs RHE) to evaluate the photoelectrochemical durability of Si@CoX2 MWs. Si@CoS2 electrode showed no photoresponse after the chronoamperometry test because it was etched through the electrolyte. By contrast, the photocurrent density of Si@CoSe2 MWs gradually increased to -5 mA cm(-2) after chronoamperometry characterization owing to the amorphous structure generation.