Carbonaceous Anodes Derived from Sugarcane Bagasse for Sodium-Ion Batteries
(2019-05-21)
Rath, Purna Chandra
;
Patra, Jagabandhu
;
Huang, Hao-Tzu
;
Bresser, Dominic
;
Wu, Tzi-Yi
To realize the sustainability of Na-ion batteries (NIBs) for large-scale energy storage applications, a resource-abundant and cost-effective anode material is required. In this study, sugarcane bagasse (SB), one of the most abundant types of biowaste, is chosen as the carbon precursor to produce a hard carbon (HC) anode for NIBs. SB has a great balance of cellulose, hemicellulose, and lignin, which prevents full graphitization of the pyrolyzed carbon but ensures a sufficiently ordered carbon structure for Na+ transport. Compared with HC derived from waste apples, which are pectin-rich and have less cellulose than SB, SB-derived HC (SB-HC) has fewer defects and a lower oxygen content. SB-HC thus has a higher first-cycle sodiation/desodiation coulombic efficiency and better cycling stability. In addition, SB-HC has a unique flake-like morphology, which can shorten the Na+ diffusion length, and higher electronic conductivity (owing to more sp(2)-hybridized carbon), resulting in superior high-rate charge-discharge performance to apple-derived HC. The effects of pyrolysis temperature on the material characteristics and electrochemical properties, evaluated by using chronopotentiometry, cyclic voltammetry, and electrochemical impedance spectroscopy, are systematically investigated for both kinds of HC.
Composition Modulation of Ionic Liquid Hybrid Electrolyte for 5 V Lithium-Ion Batteries
(2019-11-13)
Wu, Chia-Jung
;
Rath, Puma Chandra
;
Patra, Jagabandhu
;
Bresser, Dominic
;
Passerini, Stefano
Electrolyte is a key component in high-voltage lithium-ion batteries (LIBs). Bis(trifluoromethanesulfonyl)imide-based ionic liquid (IL)/organic carbonate hybrid electrolytes have been a research focus owing to their excellent balance of safety and ionic conductivity. Nevertheless, corrosion of Al current collectors at high potentials usually happens for this kind of electrolyte. In this study, this long-standing problem is solved via the modulation of the IL/carbonate ratio and LiPF6 concentration in the hybrid electrolyte. The proposed electrolyte suppresses Al dissolution and electrolyte oxidation at 5 V (vs Li+/Li) and thus allows for ideal lithiation/delithiation performance of a high-voltage LiNi0.5Mn1.5O4 (LNMO) cathode even at 55 degrees C. The underlying mechanism is examined in this work. Excellent cycling stability (97% capacity retention) for an LNMO cathode after 300 cycles is achieved. This electrolyte shows good wettability toward a polyethylene separator and low flammability. In addition, satisfactory compatibility with both graphite and Si-based anodes is confirmed. The proposed electrolyte design strategies have great potential for applications in high-voltage LIBs.
Manipulation of Nitrogen-Heteroatom Configuration for Enhanced Charge-Storage Performance and Reliability of Nanoporous Carbon Electrodes
(2020-07-22)
Sutarsis
;
Patra, Jagabandhu
;
Su, Ching-Yuan
;
Li, Ju
;
Bresser, Dominic
In this study, various nitrogen-containing functional groups, namely, pyridine (N-6), pyrrole (N-5), oxidized N (N-O), and quaternary N (N-Q), are created on activated carbon (AC) surface via melamine, ammonia, and nitric oxide doping methods. N-5 and N-6 groups markedly alter the specific surface area and pore size of AC. N-O is found to affect electrolyte wettability, and the N-Q content is closely associated with AC electronic conductivity. The nitrogen-containing groups do not contribute to pseudocapacitance in propylene carbonate and acetonitrile electrolytes. However, the nitric-oxide-treated carbon (AC-NO) exhibits the best highrate charge-discharge performance among the investigated materials. The N-Q-enriched and N-5/N-6-depleted AC-NO most effectively suppresses the leakage current and gas evolution of supercapacitors. Online gas chromatography is used to analyze the gaseous species produced from AC electrodes. With an appropriate surface functionality on carbon, the cell voltage can be increased to similar to 3 V, increasing the energy and power densities. The aging behavior of the carbon electrodes with and without nitrogen modification after being floated at 2.5 V and 70 degrees C for 3 days is investigated. An effective strategy for enhancing supercapacitor performance and reliability is proposed.