Defect induced ferromagnetic ordering in epitaxial Zn0.95Mn0.05O films on sapphire (0001)
(2019-12-04)
Liu, Wei-Rein
;
Pao, Chih-Wen
;
Yu, Doris Weijyun
;
Chin, Yi-Ying
;
Wu, Wen-Bin
We report the influence of Mn dopant on magnetic properties of Zn0.95Mn0.05O (ZMO)/Al2O3(0001) hetero-epitaxial systems grown by using pulsed-laser deposition. The room temperature (RT) intrinsic ferromagnetic (FM) ordering verified by superconducting quantum interference device magnetometer and x-ray magnetic circular dichroism spectrum of Mn L-2(,3) edges is ascribed to the substitutional Mn atoms in the Zn site of ZnO. Mn in ZMO has a tetrahedral local symmetry instead of the octahedral symmetry of MnO, after verifying the absence of the Mn-related impurities or clusters in ZMO epitaxial film by Mn K-edge and Zn K-edge x-ray absorption spectroscopy spectrum, as well as the analysis of long-range structural ordering on Renninger scan of forbidden (0005) reflection in x-ray diffraction, transmission electron microscopy and Raman spectrum. Comparison of x-ray absorption spectra of ZMO with those of ZnO epilayers at O K-, Zn K-, and L-3-edges indicates that the substitution of the Zn site with Mn enhances the charge-transfer (CT) transition and the presence of Zn vacancies (V-Zn) also dominate the photoluminescence (PL) spectrum, implying that the formation of numerous V-Zn defects plays an important role in activating FM interactions. The strong CT effect and the existence of high-density V-Zn suggest that the intrinsic RT FM ordering of insulating ZMO is a result of the formation of the bound magnetic polarons (BMPs) that interact with each other via intermediate magnetic impurities.
p-type Mesoscopic Nickel Oxide/Organometallic Perovskite Heterojunction Solar Cells
(2014-04-23)
Wang, Kuo-Chin
;
Jeng, Jun-Yuan
;
Shen, Po-Shen
;
Chang, Yu-Cheng
;
Diau, Eric Wei-Guang
In this article, we present a new paradigm for organometallic hybrid perovskite solar cell using NiO inorganic metal oxide nanocrystalline as p-type electrode material and realized the first mesoscopic NiO/perovskite/[6,6]-phenyl C61-butyric acidmethyl ester (PC61BM) heterojunction photovoltaic device. The photo-induced transient absorption spectroscopy results verified that the architecture is an effective p-type sensitized junction, which is the first inorganic p-type, metal oxide contact material for perovskite-based solar cell. Power conversion efficiency of 9.51% was achieved under AM 1.5 G illumination, which significantly surpassed the reported conventional p-type dye-sensitized solar cells. The replacement of the organic hole transport materials by a p-type metal oxide has the advantages to provide robust device architecture for further development of all-inorganic perovskite-based thin-film solar cells and tandem photovoltaics.