Enhanced photovoltaic performance with co-sensitization of porphyrin and an organic dye in dye-sensitized solar cells
(2012-04-01)
Lan, Chi-Ming
;
Wu, Hui-Ping
;
Pan, Tsung-Yu
;
Chang, Chia-Wei
;
Chao, Wei-Shan
We designed a stepwise approach for co-sensitization of a zinc porphyrin sensitizer (LD12) with a spirally configured organic dye (CD5) for dye-sensitized solar cells. The co-sensitized LD12 + CD5 device showed significantly enhanced V-OC and J(SC) relative to its individual single-dye sensitized devices. Upon optimization, the device made of the LD12 + CD5 system yielded J(SC)/mA cm(-2) = 16.7, V-OC/V = 0.74, FF = 0.73 and eta = 9.0%; this performance is superior to that of either individual device made from LD12 (eta = 7.5%) and CD5 (eta = 5.7%) under the same conditions of fabrication. To understand the effects of the potential shift and charge recombination on the cell performance, we measured charge-extraction (CE) and intensity-modulated photovoltage spectra (IMVS). Upon sensitization with each dye, the TiO2 potentials are similar, but co-sensitization causes the potential to shift down (cathodic shift). Charge recombination was significantly retarded for the co-sensitized system relative to each individual dye-sensitized system, to account for the enhanced V-OC for the former relative to the latter. A test of stability indicates a systematic trend between the LD12 + CD5 and LD12 devices; the performance of the co-sensitized device degraded only similar to 15% and remained stable during the period of 500-1000 h near 295 K.
Molecular engineering of cocktail co-sensitization for efficient panchromatic porphyrin-sensitized solar cells
(2012-12-01)
Wu, Hui-Ping
;
Ou, Zih-Wei
;
Pan, Tsung-Yu
;
Lan, Chi-Ming
;
Huang, Wei-Kai
Co-sensitization of two or more dyes with complementary absorption spectra on a semiconductor film is an effective approach to enhance the performance of a dye-sensitized solar cell (DSSC). Porphyrin sensitizer YD2-oC8 showed outstanding photovoltaic performance co-sensitized with an organic dye to cover the entire visible spectral region, 400-700 nm. To promote the light-harvesting capability beyond 700 nm, a porphyrin dimer (YDD6) was synthesized for a co-sensitized system. We report a systematic approach for engineering of molecular co-sensitization of TiO2 films in a cocktail solution containing YD2-oC8, an organic dye (CD4) and YDD6 in a specific molar ratio to optimize the photovoltaic performance of the device. The resulting device showed panchromatic spectral features in the IPCE action spectrum in the region 400-700 nm attaining efficiencies of 75-80%; the spectrum is extended to the near-IR region attaining 40-45% in 700-800 nm region, giving J(SC)/mA cm(-2) = 19.28, V-OC/mV = 753, FF = 0.719, and eta = 10.4% under standard AM 1.5 G one-sun irradiation. This performance is superior to what is obtained from the individual single-dye devices and the two-dye co-sensitized systems. The shifts of TiO2 potential upon dye uptake and the kinetics of charge recombination were examined through measurements of the charge extraction (CE) and intensity-modulated photovoltage spectroscopy (IMVS), respectively. Five co-sensitized systems were investigated to demonstrate that suppression of dye aggregation of YDD6 in the co-sensitized film is a key factor to further improve the device performance.
Spirally configured cis-stilbene/fluorene hybrids as bipolar, organic sensitizers for solar cell applications
(2012)
Chao, Wei-Shan
;
Liao, Ken-Hsien
;
Chen, Chien-Tien
;
Huang, Wei-Kai
;
Lan, Chi-Ming
Hybrids based on a dibenzosuberene core bearing a spiro-fluorene junction at the C-5 position and with amino donor and beta-thiophenyl-alpha-cyanoacrylic acid acceptor groups at C-3 and C-7, respectively, serve as new organic sensitizer materials for solar cell applications. Solar cell devices based on these materials show a conversion efficiency (eta) of up to 6.1% (V-oc = 697 mV, J(sc) = 12.2 mA cm(-2), FF = 0.72) under AM 1.5 G conditions. The best IPCE values exceed 75% within the 450-550 nm absorption range.