In Situ Analysis of Growth Behaviors of Cu2O Nanocubes in Liquid Cell Transmission Electron Microscopy
(2019-08-06)
Lin, Ya-Hsuan
;
Chen, Jui-Yuan
;
Chen, Fu-Chun
;
Kuo, Ming-Yu
;
Hsu, Yung-Jung
Metal oxides have attracted substantial attention over the years and are commonly used in the semiconductor industry because of their excellent physical and chemical properties. Among the various metal oxides, cuprous oxide (Cu2O) is regarded as a promising material. It is inexpensive, earth-abundant, and nontoxic; therefore, it can be used in catalysis, sensors, solar cells, and p-type semiconductors. However, the redox reaction of Cu2O is still uncertain. The size, morphology, and structure of Cu2O strongly influence its properties. In this work, we developed a new synthesis method of Cu2O that involves reducing the precursor by an electron beam without reducing agent. The growth process of Cu2O nanocubes was observed via in situ liquid cell transmission electron microscopy (in situ LCTEM). The nucleation kinetics, oscillating growth behavior, and redox reaction of the Cu2O nanocubes in the liquid phase were systematically studied. Cu2O exhibited a round shape at the beginning and transformed into a cubic shape afterward. Interestingly, the Cu2O nanocubes grew clearly under long-term observation; however, their diameters increased and fluctuated during the short-term observation. The electron beam not only stimulated the solution to reduce the nanocubes but also caused electron radiation effect to the nanocubes. During the Cu2O growth and dissolution, the cubic shape evolved with specific planes in the {100} family. Our direct observation sheds light on the preparation of Cu2O by a reduction method, extending the study of reaction kinetics and providing a new way to synthesize metal oxides.
In situ TEM observation of Au-Cu2O core-shell growth in liquids
(2019-06-07)
Chen, Fu-Chun
;
Chen, Jui-Yuan
;
Lin, Ya-Hsuan
;
Kuo, Ming-Yu
;
Hsu, Yung-Jung
Heterogeneous nanoparticles are widely used in catalysis, sensors and biology due to their versatile functions. Among the various heterogeneous nanoparticles, Au-Cu2O core-shell nanoparticles show high stability and short response times for use as sensors and catalysts and have thus attracted much attention. Previous studies show that the properties of Au-Cu2O are mainly related to the shape and size of the Au-Cu2O nanoparticles. However, the forming behavior of heterostructures and the mechanism have not been fully explored. In this work, liquid cell transmission electron microscopy (LCTEM) was used to investigate the formation of these interesting Au-Cu2O nanoparticles and their process of aggregation. The electron beam and dispersion of gold nanoparticles are both important parameters for the reduction reaction in in situ LCTEM. The Au-Cu2O core-shell nanoparticles can be synthesized to have two morphologies, multifaceted and cubic. The nanoparticles grew into these different morphologies due to the amount of remaining citrate ligands on the surface of the gold nanoparticles. For the multifaceted nanoparticles, the epitaxy of the two components is confirmed from high-resolution TEM images and electron diffraction patterns with an epitaxial relationship of Au (020)//Cu2O (020) and Au [101]//Cu2O [101]. The growth rate is approximately 210 nm(2) s-1. On the other hand, the cubic nanoparticles nucleate and grow independently. The growth kinetics and elemental distributions have been systematically studied. In addition, the nanoclusters would float, rotate, and finally aggregate with the surrounding clusters. This in situ experiment sheds light on the growth mechanisms of nanostructures and will improve the applicability and controllability of heterostructure synthesis.