Cs0.33WO3 compound nanomaterial-incorporated thin film enhances output of thermoelectric conversion in ambient temperature environment
(2018-06-01)
Cheng, Chih-Yi
;
Chen, Guan-Lin
;
Hu, Po-Sheng
;
光電系統研究所
;
照明與能源光電研究所
Cs0.33WO3 nanomaterial absorbs a range of near-infrared (NIR) wavelength spanning 900-2400 nm, of which the main contributor of heat energy may be utilized for electrical generation. In this research, the capability of Cs0.33WO3 nanomaterial in enhancing the output of a thermoelectric (TE) device by trapping the absorbed heat at the hot-side surface of the device is investigated. The material is synthesized through a combination of the processes of co-precipitation and wet nano-grinding, and the characterization of its structural and optical properties was carried out using X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and visible-near-infrared absorption spectroscopy. Likewise, the photothermal property of Cs0.33WO3 nanomaterial, in the form of solution or solid film, is assessed to gain better insight into its effects on the electrical output of the TE device, utilizing a laser with wavelength of 808 nm, a solar simulator, and sunlight in ambient environment. Moreover, the photoelectric property of the Cs0.33WO3 nanomaterial-incorporated TE device was evaluated in four different types of weather condition, sunny, sunny with partly cloudy, cloudy, and rainy; and our results indicate that Cs0.33WO3 nanomaterial is capable of enhancing the output of thermoelectric conversion in an ambient environment. In a complete sunny day, when compared with a bare thermoelectric device, the coating of Cs0.33WO3 nanomaterial with concentration of 0.66 wt% demonstrated a rise of 13.1% in the maximal attainable temperature and a corresponding increase of 291% in maximal output voltage.
Tuning visible-wavelength spectrum of white-light super-continuum via etalon transmission in lamellar ZnO micro/nanoparticle-stacked structures
(2019-10-01)
Hu, Po-Sheng
;
Chen, Guan-Lin
;
Wu, Cheng-En
;
光電系統研究所
;
影像與生醫光電研究所
Multi-layered micro/nanostructures enable the fine-tuning of spectral bandwidth induced by coherent interference of multi-scattering and refraction bounded by a motive of Fabry Perot etalon. In this paper a ZnO micro/nanostructured thin film device is grown on a 21 nm silver film-sputtered sapphire substrates (0001) and attempted to be complied as a transmission-mode white-light spectrum tuning device. In details, the growth of the structures as a function of temporal duration and the effects of deposition of a 21 nm silver film atop sapphire substrates to the structural and optical properties of ZnO structures are investigated. Results of SEM imaging reveals that the insertion of the silver film enables synthesis of round ZnO particles at micro or nanoscales depending on the duration of growth time as opposed to the floral pattern associated with plain sapphire substrates. Characterizing material crystallization by XRD spectra found one dominant and two minor peaks along the planes of crystallization (002), and (100) and (101), correspondingly. Also, the characteristic PL peak at 380 nm was confirmed when excited at 325 nm, and the intensity decreases as the duration of growth time increases. Finally, growth duration-dependent modulation of peak wavelength and spectral bandwidth of the continuum laser was demonstrated.
Zno Micro/Nanostructures Grown on Sapphire Substrates Using Low-Temperature Vapor-Trapped Thermal Chemical Vapor Deposition: Structural and Optical Properties
(2018-01-01)
Hu, Po-Sheng
;
Wu, Cheng-En
;
Chen, Guan-Lin
;
光電系統研究所
;
影像與生醫光電研究所
In this research, the Zn(C5H7O2)(2)center dot xH(2)O-based growth of ZnO micro/nanostructures in a low temperature, vapor-trapped chemical vapor deposition system was attempted to optimize structural and optical properties for potential biomedical applications. By trapping in-flow gas molecules and Zinc vapor inside a chamber tube by partially obstructing a chamber outlet, a high pressure condition can be achieved, and this experimental setup has the advantages of ease of synthesis, being a low temperature process, and cost effectiveness. Empirically, the growth process proceeded under a chamber condition of an atmospheric pressure of 730 torr, a controlled volume flow rate of input gas, N-2/O-2, of 500/500 Standard Cubic Centimeters per Minute (SCCM), and a designated oven temperature of 500 degrees C. Specifically, the dependence of structural and optical properties of the structures on growth duration and spatially dependent temperature were investigated utilizing scanning electron microscopy, X-ray diffraction (XRD), photoluminescence (PL), and ultraviolet-visible transmission spectroscopy. The experimental results indicate that the grown thin film observed with hexagonal structures and higher structural uniformity enables more prominent structural and optical signatures. XRD spectra present the dominant peaks along crystal planes of (002) and (101) as the main direction of crystallization. In addition, while the structures excited with laser wavelength of 325 nm emit a signature radiation around 380 nm, an ultraviolet lamp with a wavelength of 254 nm revealed distinctive photoluminescence peaks at 363.96 nm and 403.52 nm, elucidating different degrees of structural correlation as functions of growth duration and the spatial gradient of temperature. Transmittance spectra of the structures illustrate typical variation in the wavelength range of 200 nm to 400 nm, and its structural correlation is less significant when compared with PL.