Browsing by Author "Chen, Jebb-Fang"

Now showing 1 - 2 of 2

Effect of AlInGaN barrier layers with various TMGa flows on optoelectronic characteristics of near UV light-emitting diodes grown by atmospheric pressure metalorganic vapor phase epitaxy
(2011-08-01)
Fu, Yi-Keng
;
Lu, Yu-Hsuan
;
Jiang, Ren-Hao
;
Chen, Bo-Chun
;
Fang, Yen-Hsiang
Near ultraviolet light-emitting diodes (LEDs) with quaternary AlInGaN quantum barriers (QBs) are grown by atmospheric pressure metalorganic vapor phase epitaxy. The indium mole fraction of AlInGaN QB could be enhanced as we increased the TMG flow rate. Both the wavelength shift in EL spectra and forward voltage at 20 mA current injection were reduced by using AlInGaN QB. Under 100 mA current injection, the LED output power with Al(0.089)In(0.035)Ga(0.876)N QB can be enhanced by 15.9%, compared to LED with GaN QB. It should be attributed to a reduction of lattice mismatch induced polarization mismatch in the active layer. Crown Copyright (C) 2011 Published by Elsevier Ltd. All rights reserved.
Study of InGaN-Based Light-Emitting Diodes on a Roughened Backside GaN Substrate by a Chemical Wet-Etching Process
(2011-10-01)
Fu, Yi-Keng
;
Chen, Bo-Chun
;
Fang, Yen-Hsiang
;
Jiang, Ren-Hao
;
Lu, Yu-Hsuan
The InGaN-based light-emitting diodes (LEDs) with a roughened backside on the N-face surface of GaN substrate were fabricated through a chemical wet-etching process to increase light-extraction efficiency. The stable crystallographic etching planes were formed as the GaN {10 (11) over bar} planes. When the near-ultraviolet and blue LED were operated as a forward current of 20 mA, the output power of LEDs was improved from 13.2 and 19.9 mW to 25.6 and 24.0 mW, respectively. The different enhanced ratio is attributed to the different transmittance as a function of wavelength is caused from hexagonal pyramid on N-face GaN substrate after wet-etching process.