Demonstration of 40-nm Channel Length Top-Gate p-MOSFET of WS2 Channel Directly Grown on SiOx/Si Substrates Using Area-Selective CVD Technology
(2019-12-01)
Chung, Yun-Yan
;
Lu, Kuan-Cheng
;
Cheng, Chao-Ching
;
Li, Ming-Yang
;
Lin, Chao-Ting
For high-volume manufacturing of 2-D transistors, area-selective chemical reaction deposition (CVD) growth is able to provide good-quality 2-D layers and may be more effective than exfoliation from bulk crystals or wet/dry transfer of large-area as-grown 2-D layers. We have successfully grown continuous and uniform WS2 film comprising around seven layers by area-selective CVD approach using patterned tungsten source/drain metals as the seeds. The growth mechanism is inferred and supported by the transmission electron microscope (TEM) images, as well. The first top-gate MOSFETs of CVD-WS2 channels on SiOx/Si substrates are demonstrated to have good short channel electrical characteristics: ON-/OFF-ratio of 10(6), a subthreshold swing of 97 mV/decade, and nearly zero drain-induced barrier lowering (DIBL).
First demonstration of 40-nm channel length top-gate WS2 pFET using channel area-selective CVD growth directly on SiOx/Si substrate
(2019-01-01)
Cheng, Chao-Ching
;
Chung, Yun-Yan
;
Li, Ming-Yang
;
Lin, Chao-Ting
;
Li, Chi-Feng
Area-selective channel material growth for 2D transistors is more desirable for volume manufacturing than exfoliation or wet/dry transfer after large area growth. We demonstrate the first top-gate WS(2)p-channel field-effect transistors (p-FETs) fabricated on SiOx/Si substrate using channel area-selective CVD growth. Smooth and uniform WS2 comprising approximately 6 layers was formed by area-selective CVD growth in which a patterned tungsten-source/drain served as the seed for WS2 growth. For a 40 nm gate length transistor, the device has impressive electrical characteristics: on/off ratio of similar to 10(6), a S.S. of similar to 97 mV/dec.. and nearly zero DIBL.