Catalytically solid-phase self-organization of nanoporous SnS with optical depolarizability
(2016)
Cheng, Chih-Hsien
;
Chi, Yu-Chieh
;
Wu, Chung-Lun
;
Lin, Chun-Jung
;
Tsai, Ling-Hsuan
The catalytic solid-phase synthesis of self-organized nanoporous tin sulfide (SnS) with enhanced absorption, manipulative transmittance and depolarization features is demonstrated. Using an ultralow radio-frequency (RF) sputtering power, the variation of the orientation angle between the anodized aluminum oxide (AAO) membrane and the axis of the sputtered ion beam detunes the catalytically synthesized SnS from nanorod to nanoporous morphology, along the sidewall of the AAO membrane. The ultraslow catalytic sputtering synthesis on the AAO at the RF plasma power of 20 W and the orientation angle of 0 degrees regulates the porosity and integrality of nanoporous SnS, with average pore diameter of 80-150 nm. When transferring from planar to nanoporous structure, the phase composition changes from SnS to SnS2-Sn2S3, and the optical bandgap shrinks from 1.43 to 1.16 eV, due to the preferred crystalline orientation, which also contributes to an ultralow reflectance of <1% at 200-500 nm when both the transmittance and the surface scattering remain at their maxima. The absorption coefficient is enhanced by nearly one order of magnitude with its minimum of >5 x 10(4) cm(-1) at the wavelength between 200 and 700 nm, due to the red-shifting of the absorption spectrum to at least 100 nm. The catalytically self-organized nanoporous SnS causes strong haze and beam divergence of 20 degrees-30 degrees by depolarized nonlinear scattering at the surface, which favors the solar energy conversion with reduced surface reflection and enhanced photon scattering under preserved transmittance.
Transferring the bendable substrateless GaN LED grown on a thin C-rich SiC buffer layer to flexible dielectric and metallic plates
(2017-01-21)
Cheng, Chih-Hsien
;
Huang, Tzu-Wei
;
Wu, Chung-Lun
;
Chen, Mu Ku
;
Chu, Cheng Hung
By growing an epitaxial GaN LED on C-rich a-SiC buffer deposited SiO2/Si substrate, the simplified transfer to versatile flexible metallic/dielectric membranes is demonstrated. Both the high growth temperature at 1000 degrees C and the slow deposition rate played important roles in the meticulous MOCVD growth of n-GaN along the surface normal of the a-SiC at the very beginning. High substrate temperature facilitated the refinement of C-rich SiC buffer from amorphous to partially crystalline with (0004)-orientation, which effectively reduces the lattice mismatch between n-GaN and SiC at the interface so as to gradually improve the crystalline n-GaN regrowth. The substrateless GaN LED transferred to flexible copper plates showed reduced turn-on voltage of 2.6 V, enhanced output power of 370 mW, enlarged power-to-current slope of 1.24 W A(-1), increased external quantum efficiency of 45%, and reduced efficiency droop of 15% under a bias of 300 mA. The thermal conductivity of the transferred substrate affected the EL peak wavelength shift of the substrateless GaN LED on SiC buffer. Heating the GaN LED on flexible copper plate to 65 degrees C only reduced its power by 10% and red-shifted its wavelength by 1 nm under a bias at 100 mA; the Auger effect resulted in a degraded EQE of 39.1% and an enlarged EQE droop of 8.5%. Bending the surface diameter of the curvature of the copper plate to 1.2 cm decayed the output power by 12% and red-shifted the EL peak by 5 nm because of the lattice strain induced quantum confined Stark effect (QCSE). Such a bendable substrateless GaN LED transferred to flexible membrane with superior heat dissipation and bending tolerance is a desired lighting element for green photonics in this era.