Demonstration of 40-nm Channel Length Top-Gate p-MOSFET of WS2 Channel Directly Grown on SiOx/Si Substrates Using Area-Selective CVD Technology
(2019-12-01)
Chung, Yun-Yan
;
Lu, Kuan-Cheng
;
Cheng, Chao-Ching
;
Li, Ming-Yang
;
Lin, Chao-Ting
For high-volume manufacturing of 2-D transistors, area-selective chemical reaction deposition (CVD) growth is able to provide good-quality 2-D layers and may be more effective than exfoliation from bulk crystals or wet/dry transfer of large-area as-grown 2-D layers. We have successfully grown continuous and uniform WS2 film comprising around seven layers by area-selective CVD approach using patterned tungsten source/drain metals as the seeds. The growth mechanism is inferred and supported by the transmission electron microscope (TEM) images, as well. The first top-gate MOSFETs of CVD-WS2 channels on SiOx/Si substrates are demonstrated to have good short channel electrical characteristics: ON-/OFF-ratio of 10(6), a subthreshold swing of 97 mV/decade, and nearly zero drain-induced barrier lowering (DIBL).
Design Space Analysis for Cross-Point 1S1MTJ MRAM: Selector-MTJ Cooptimization
(2020-08-01)
Chiang, Hung-Li
;
Chen, Tzu-Chiang
;
Song, Ming-Yuan
;
Chen, Yu-Sheng
;
Chiu, Jung-Piao
To increase the density of magnetoresistive random accessmemory (MRAM) beyond the 1T1MTJMRAM cell in use today, the design space for 1S1MTJ MRAM array is analyzed by cooptimizing both selectors and MTJs. Current low-resistance MTJs for 1T1MTJ MRAM are not suitable for 1S1MTJ MRAM. Threshold-type selectors would induce a strong read disturb on the MTJ due to the snapback voltage (V-TH-V-HOLD) when the selector is turned on. Also, exponential-type selectorswould degrade the read margin (RM) due to its large ON-state resistance. When using existing selectors to achieve a 1-M-bit 1S1MTJ array, it is necessary to adjust the product of resistance and area (RA) and the diameter of the MTJ. An MTJ with the RA = 15 Omega . mu m(2) and the diameter = 50 nm can meet the criterion of RM > 10% for both exponential-type selectors (exponential slope = 300-500 mV/decade with the current density similar to 1 MA/cm(2)) and threshold-type selectors (V-TH-V-HOLD similar to 250 mV). A design space accommodating a selector variation of around 1% can be found for MTJs with tunnel magnetoresistance ratio (TMR) < 250%. With an increased TMR of 250%-350% of the MTJ, the tolerance of variations for exponential-type selectors and threshold-type selectors can be improved to 2% and 4%, respectively. This provides a chance for the 1S1MTJ MRAM with existing selectors.
First demonstration of 40-nm channel length top-gate WS2 pFET using channel area-selective CVD growth directly on SiOx/Si substrate
(2019-01-01)
Cheng, Chao-Ching
;
Chung, Yun-Yan
;
Li, Ming-Yang
;
Lin, Chao-Ting
;
Li, Chi-Feng
Area-selective channel material growth for 2D transistors is more desirable for volume manufacturing than exfoliation or wet/dry transfer after large area growth. We demonstrate the first top-gate WS(2)p-channel field-effect transistors (p-FETs) fabricated on SiOx/Si substrate using channel area-selective CVD growth. Smooth and uniform WS2 comprising approximately 6 layers was formed by area-selective CVD growth in which a patterned tungsten-source/drain served as the seed for WS2 growth. For a 40 nm gate length transistor, the device has impressive electrical characteristics: on/off ratio of similar to 10(6), a S.S. of similar to 97 mV/dec.. and nearly zero DIBL.