Effect of Saccharose Concentration and Temperature on the Internal Stress and Corrosion Resistance of Electroplated Chromium Coatings Prepared from Chromium (III) Bath
(2020-04-01)
Sheu, Hung-Hua
;
Chen, Yuan-Rong
;
Ger, Ming-Der
;
交大名義發表
;
National Chiao Tung University
The trivalent chromium carbon coatings are electroplated from different electroplating temperature (10, 0 and -5 degrees C) and different concentration (0.01, 0.02 and 0.03 M) of saccharose (C12H22O11). The saccharose play a role of stress inhibitor in the bath during electroplating process. The results of internal stress analysis show that the internal stress of the trivalent chromium carbon coating decreases with the increase of concentration of saccharose at individual electroplating temperatures, this shows that saccharose has the effect on suppressing the accumulation of stress within the coating. Moreover, the electroplating temperature also affect the internal stress of trivalent chromium carbon coatings i.e. the lower electroplating temperature (-5 degrees C) will reduce the accumulation of stress within the coating during electroplating. The smallest internal stress of trivalent chromium carbon coatings is 13.4 MPa, electroplated at -5 degrees C with a concentration of saccharose at 0.02 M. The best i(corr) is approximately at 1.32x 10(-6) A/dm(2), this coatings is also electroplated at -5 degrees C and the concentration of saccharose at 0.02 M. The results indicated that both electroplating temperature and concentration of saccharose can reduce the internal stress within trivalent chromium carbon coatings and decrease the through-deposit cracking within coatings, thereby improving the corrosion resistance of coatings.