Efficient wavelength conversion with low operation power in a Ta2O5-based micro-ring resonator
(2017-12-01)
Wu, Chung-Lun
;
Huang, Jen-Yang
;
Ou, Ding-Hsin
;
Liao, Ting-Wei
;
Chiu, Yi-Jen
The Ta2O5-based micro-ring resonator with an unloaded quality factor of 182,000 has been demonstrated to realize efficient nonlinear wavelength generation. The propagation loss of the resonator is 0.5 cm(-1), and the buildup factor of the ring resonator is estimated to be similar to 50. With a high buildup factor of the ring structure, the four-wave-mixing (FWM) conversion efficiency of -30 dB is achieved in the resonator with a pump power of 6 mW. Based on power-dependent FWM results, the nonlinear refractive index of Ta2O5 is estimated to be 1.4x10-14 cm(2)/W at a wavelength of similar to 1550 nm. The demonstration of an enhanced FWM process in the Ta(2)O(5-)based micro-ring cavity implies the possibility of realizing FWM-based optical parametric oscillation in a Ta2O5-based micro-ring resonator. (C) 2017 Optical Society of America
Tens of GHz Tantalum pentoxide-based micro-ring all-optical modulator for Si photonics
(2017-03-01)
Wu, Chung-Lun
;
Hsieh, Cheng-Hsuan
;
Lin, Gong-Ru
;
Chi, Wen-Chun
;
Chiu, Yi-Jen
A tantalum pentoxide-based (Ta2O5-based) micro-ring alloptical modulator was fabricated. The refractive index inside the micro-ring cavity was modified using the Kerr effect by injecting a pumped pulse. The transmittance of the ring resonator was controlled to achieve all-optical modulation at the wavelength of the injected probe. When 12 GHz pulses with a peak power of 1.2 W were coupled in the ring cavity, the transmission spectrum of the Ta2O5 resonator was redshifted by 0.04 nm because of the Kerr effect. The relationship between the modulation depth and gap of the Ta2O5 directional coupler is discussed. An optimized gap of 1100 nm was obtained, and a maximum buildup factor of 11.7 with 84% modulation depth was achieved. The nonlinear refractive index of Ta2O5 at 1.55 mu m was estimated as 3.4 x 10(-14) cm(2)/W based on the Kerr effect, which is almost an order of magnitude higher than that of Si3N4. All results indicate that Ta2O5 has potential for use in nonlinear waveguide applications with modulation speeds as high as tens of GHz.