Competition Between Effects of Pore Sizes and Annealing Solvents on the Morphology Manipulation of 3D Block Copolymer Nanostructures Using Anodic Aluminum Oxide Templates
(2016-06)
Chu, Chiang-Jui
;
Chung, Pei-Yun
;
Chu, Chien-Wei
;
Cheng, Ming-Hsiang
;
Chi, Mu-Huan
In this work, the morphologies of polystyrene-block-polydimethylsiloxane (PS-b-PDMS) nanostructures using solvent-induced wetting in the nanopores of anodic aluminum oxide (AAO) templates are investigated. AAO templates with three different pore sizes (approximate to 200, approximate to 60, and approximate to 30 nm) are used in this work to differentiate the effect of confinement and annealing solvents. Different from the results by the traditional wetting methods, two major effects are identified in affecting the morphologies. At larger pore sizes, the morphologies of the nanostructures are mainly affected by the annealing solvent. At smaller pore sizes, however, the morphologies are mainly controlled by the confinement effect (pore sizes).
Reversible morphology control of three-dimensional block copolymer nanostructures by the solvent-annealing-induced wetting in anodic aluminum oxide templates
(2016)
Chu, Chiang-Jui
;
Cheng, Ming-Hsiang
;
Chung, Pei-Yun
;
Chi, Mu-Huan
;
Jeng, Kai-Sheng
In this work, the authors study the fabrication of three-dimensional block copolymer nanostructures in which the morphologies can be reversibly controlled. Polystyrene-block-polydimethylsiloxane (PS-b-PDMS), a promising candidate for nanolithography, is introduced into cylindrical nanopores of anodic aluminum oxide (AAO) templates using a solvent annealing-induced nanowetting in templates (SAINT) method. Not only the morphologies of the infiltrated PS-b-PDMS nanostructures can be tuned by the annealing solvents, but also the solvent-vapor-controlled morphologies can be altered reversibly by annealing the samples repeatedly between different solvent vapors.
Three-Dimensional Block Copolymer Nanostructures by the Solvent-Annealing-Induced Wetting in Anodic Aluminum Oxide Templates
(2014-09-01)
Chu, Chiang-Jui
;
Chung, Pei-Yun
;
Chi, Mu-Huan
;
Kao, Yi-Huei
;
Chen, Jiun-Tai
Block copolymers have been extensively studied over the last few decades because they can self-assemble into well-ordered nanoscale structures. The morphologies of block copolymers in confined geometries, however, are still not fully understood. In this work, the fabrication and morphologies of three-dimensional polystyrene-block-polydimethylsiloxane (PS-b-PDMS) nanostructures confined in the nanopores of anodic aluminum oxide (AAO) templates are studied. It is discovered that the block copolymers can wet the nanopores using a novel solvent-annealing-induced nanowetting in templates (SAINT) method. The unique advantage of this method is that the problem of thermal degradation can be avoided. In addition, the morphologies of PS-b -PDMS nanostructures can be controlled by changing the wetting conditions. Different solvents are used as the annealing solvent, including toluene, hexane, and a co-solvent of toluene and hexane. When the block copolymer wets the nanopores in toluene vapors, a perpendicular morphology is observed. When the block copolymer wets the nanopores in co-solvent vapors (toluene/hexane = 3:2), unusual circular and helical morphologies are obtained. These three-dimensional nanostructures can serve as naontemplates for refilling with other functional materials, such as Au, Ag, ZnO, and TiO2.