Enhanced Free Exciton and Direct Band-Edge Emissions at Room Temperature in Ultrathin ZnO Films Grown on Si Nanopillars by Atomic Layer Deposition
(2011-11-01)
Chang, Yuan-Ming
;
Shieh, Jiann
;
Chu, Pei-Yuan
;
Lee, Hsin-Yi
;
Lin, Chih-Ming
Room-temperature ultraviolet (UV) luminescence was investigated for the atomic layer deposited ZnO films grown on silicon nanopillars (Si-NPs) fabricated by self-masking dry etching in hydrogen-containing plasma. For films deposited at 200 degrees C, an intensive UV emission corresponding to free-exciton recombination (similar to 3.31 eV) was observed with a nearly complete suppression of the defect-associated broad visible range emission peak. On the other hand, for ZnO films grown at 25 degrees C, albeit the appearance of the defect-associated visible emission, the UV emission peak was observed to shift by similar to 60 meV to near the direct band edge (3.37 eV) recombination emission. The high-resolution transmission electron microscopy (HRTEM) showed that the ZnO films obtained at 25 degrees C were consisting of ZnO nanocrystals with a mean radius of 2 nm embedded in a largely amorphous matrix. Because the Bohr radius of free-exictons in bulk ZnO is similar to 2.3 nm, the size confinement effect may have occurred and resulted in the observed direct band edge electron-hole recombination. Additionally, the results also demonstrate order of magnitude enhancement in emission efficiency for the ZnO/Si-NP structure, as compared to that of ZnO directly deposited on Si substrate under the same conditions.
Magnetic domain studies of La0.7Sr0.3MnO3 film deposited on SrLaAlO3 (001) substrate
(2013-06-26)
Liu, Chi-Ching
;
Chu, Pei-Yuan
;
Chiang, Yao-Wei
;
Juang, Jenh-Yih
;
Jen, Shien-Uang
Epitaxial 120 nm La0.7Sr0.3MnO3 (LSMO) compressively strained thin films were deposited on single-crystalline SrLaAlO3(0 0 1) (SLAO) substrates by the pulsed laser deposition (PLD) method. From the x-ray diffraction study, we confirmed that the c-axis of the LSMO crystal pointed out of the film plane. Two kinds of magnetic experiments were performed on the film: (i) the in-plane (field H (sic) H-P) and the out-of-plane (field H (sic) H-N) magnetic hysteresis loop measurements and (ii) magnetic force microscopy scans. We have proved from both theory and experiment that the LSMO film should exhibit the weak and tilted perpendicular magnetic anisotropy at room temperature (RT), that is, the easy axis (EA) is tilted relative to the film normal by an angle theta(o) is approxiamtely equals to 37 degrees, when the film is in the demagnetized state. The magnetic domain (MD) structure of the demagnetized LSMO film showed a maze-like pattern. Although from the in-plane hysteresis loop, H-P = 600 Oe seems large enough to saturate the film, the corresponding MD structure was not in a single-domain state. Instead, there were two types of MDs: the canted MD and the saturated MD. The MD patterns of the LSMO film between the demagnetized and the remanent states were different. In addition, there were double-switch phenomena in the out-of-plane hysteresis loop. When vertical bar H-N vertical bar congruent to 140 Oe, a transition of the MD pattern from the maze-like to the closure (or dense-stripe) type occurred.