A Study of the Relationship Between Endurance and Retention Reliability for a HfOx-Based Resistive Switching Memory
(2020-09-01)
Chung, Wei-Min
;
Chang, Yao-Feng
;
Hsu, Yu-Lin
;
Chen, Y. -C. Daphne
;
Lin, Chao-Cheng
This study determines the relationship between retention and endurance reliability for a HfOx-based resistive random access memory (ReRAM). A TiN (15 nm) / HfOx (6 nm) / Ti (10 nm) / TiN (40 nm) stacked structure is fabricated and tested to verify its basic characteristics and reliability. The high resistance states (HRS) retention behavior is characterized and is found to degrade over 100x on the endured bits because there is a sequential high temperature procedure. The degradation is reduced slightly to a similar to 30x drop for the endured devices with one single refresh cycle. During the endurance and retention test procedures, the HRS resistance decreases because neutral oxygen vacancy filaments grow and this cannot be reversed. The I-V characteristics for endured devices are also determined. The results show that isothermal treatment causes a gradual SET and RESET process with multiple feasible states. The thermally induced filament degradation model (isolated filament vs. continuous filament) is verified by the relationship between retention and endurance reliability. Design guidance is recommended for an improvement in ReRAM reliability.
SiCxNy-based resistive and threshold switching by using single precursor plasma-enhanced atomic layer deposition
(2020-05-26)
Hsu, Yu-Lin
;
Chang, Yao-Feng
;
Chung, Wei-Min
;
Chen, Ying-Chen
;
Lin, Chao-Cheng
In this work, SiCxNy-based resistive switching memory by using a single precursor for the back end of line (BEOL) integration has been investigated. SiCxNy films were deposited on the aluminum (Al) substrates using plasma enhanced atomic layer deposition (PEALD) method. The effects of SiCxNy chemical structure with respect to resistive switching characteristics have been studied, and the results suggest that the resistive switching mechanism is dominated by the interfacial Schottky junction with SiCxNy composition. This work not only demonstrates a PEALD method in fabricating SiCxNy-based electronics active devices but also provides additional insights into the interaction between the electrical and chemical structures in bi-functional resistive switching or threshold switching behavior. A demonstrated PEALD tool with simple single-precursor for SiCxNy deposition shows excellent feasibility to be used as functional memory and selector devices, further giving the potential pathway for advanced BEOL process integration.