Improvement of Crystalline and Photoluminescence of Atomic Layer Deposited m-Plane ZnO Epitaxial Films by Annealing Treatment
(2012-10-01)
Yang, S.
;
Lin, B. H.
;
Kuo, C. C.
;
Hsu, H. C.
;
Liu, W-R
Monocrystalline m-plane ZnO epitaxial films with flat surface morphology were grown on m-plane sapphire by using atomic layer deposition. X-ray diffraction and transmission electron microscopy measurements verify not only the in-plane epitaxial relationship of the as-grown films as (10 (1) over bar0)< 0001 >(ZnO)parallel to(10 (1) over bar0)<(1) over bar2 (1) over bar0 > Al2O3 but also the absence of domains with undesirable orientations, which are generally obtained in the m-plane ZnO films grown by other methods. Experimental results indicate that the basal plane stacking fault (BSF) is the dominant structural defects that contribute to the emission at 3.31 eV in m-plane ZnO films. Exactly how thermal annealing affects the structural and optical properties of ZnO epi-films was also investigated. Additionally, based on time-resolved photoluminescence at 5 K, the decay time of BSF related emission and near-band-edge (NBE) emission were determined. Results of this work further demonstrated that the decay time of NBE emission increases with a higher annealing temperature, accompanied by an improvement in crystal structure.
Recombination dynamics of a localized exciton bound at basal stacking faults within the m-(p)lane ZnO film
(2014-07-07)
Yang, S.
;
Hsu, H. C.
;
Liu, W-R.
;
Lin, B. H.
;
Kuo, C. C.
We investigated the carrier dynamics near basal stacking faults (BSFs) in m-plane ZnO epitaxial film. The behaviors of the type-II quantum wells related to the BSFs are verified through time-resolved and time-integrated photoluminescence. The decay time of the emission of BSFs is observed to have a higher power law value and longer decay time than the emission of the donor-bound excitons. The spectral-dependent decay times reveal a phenomenon of carriers migrating among band tail states, which are related to the spatial distribution of the type-II quantum wells formed by the BSFs. A high density of excited carriers leads to a band bending effect, which in turn causes a blue-shift of the emission peak of BSFs with a broadened distribution of band tail states. (C) 2014 AIP Publishing LLC.