Gold Nanoparticle-Assisted Laser Surface Modification of Borosilicate Glass Substrates
(2009-12-03)
Hashimoto, Shuichi
;
Uwada, Takayuki
;
Hagiri, Masahide
;
Takai, Hiroaki
;
Ueki, Tomoyuki
This paper describes the photomodification of borosilicate glass substrates assembled with 40 nm diameter gold nanoparticles (Au NPs) with surface coverages ranging from 17 to 23% on excitation of the localized surface plasmon band of the NPs with a 532 nm nanosecond pulsed-laser beam. The laser irradiation allowed the splitting and fusion of NPs on the substrate surface and, at the same time, the formation of craters of less than 10 nm diameter at various places following one laser shot with a relatively high intensity of 460 or 370 mJ.cm(-2).pulse(-1) but well below the breakdown threshold of 25-40 J.cm(-2).pulse(-1). The formation of the craters was more and more distinctly observed by continuous irradiations. The number density, average diameter, and the surface coverage of the craters were not linearly dependent on the laser shot number but exhibited the saturation behavior due to the consumption of Au NPs. The threshold laser energy for the crater formation was dependent on the accumulated number of laser shots: a greater number of laser shots were necessary to form craters as the laser fluence decreases. Most interestingly, the laser-irradiated areas of the substrate exhibited a greater susceptibility to the wet chemical etching with aqueous hydrogen fluoride. The mechanism of the laser modification and a possible application to nanofabrication on glass surfaces by utilizing Au NPs were discussed on the basis of the scanning electron microscopy (SEM) observation as well as the extinction and light scattering spectroscopic measurements.
Mechanistic Aspect of Surface Modification on Glass Substrates Assisted by Single Shot Pulsed Laser-Induced Fragmentation of Gold Nanoparticles
(2011-03-31)
Hashimoto, Shuichi
;
Uwada, Takayuki
;
Hagiri, Masahide
;
Shiraishi, Ryowya
;
應用化學系
This paper describes the mechanistic investigation on the photomodification of a borosilicate glass substrate assembled with 47 +/- 8 nm gold nanoparticles and exposed to a single shot of 532 nm nanosecond pulsed-laser light. The laser fluences ranging from 180 to 430 mJ cm(-2) pulse(-1), the values of which are 2 orders of magnitude lower than the breakdown threshold of quartz of 15-20 J cm(-2) pulse(-1) were used. Upon photomodification, the craters of similar to 20 nm diameter and similar to 10 tun depth were formed on the glass surface simultaneously with the laser-induced splitting of Au nanopartides to generate smaller particles of 15 nm diameter. The number density of the craters increased depending on the laser fluence with a sharp rise, the onset of which occurred at similar to 160-170 mJ cm(-2) pulse(-1), and reached a value of twice the number density of original Au particles (150 +/- 10 particles mu m(-2)) with a weak tendency to level off at high fluences. The onset of the crater formation coincides with splitting of gold nanopartides due to the temperature rise above the boiling point of gold resulting from the absorption of the laser energy. Thus, the explosive evaporation of gold nanoparticles is postulated to play a crucial role for the modification observed here. This assumption gained a solid support from the estimation of laser fluence-dependent thermoacoustic pressures due to the sudden evaporation of gold. This finding may represent a new application of the laser ablation/fragmentation of nanoparticles to material processing.