Mechanical behavior and electrochemical stability of gas-nitrided FeMnAlC alloy in simulated body fluid
(2018-04-01)
Hsueh, Shun-Jen
;
Huang, Jhen-Yi
;
Chao, Chuen-Guang
;
Juang, Jenh-Yih
;
Liu, Tzeng-Feng
The mechanical performance and electrochemical stability in simulated body fluid (SBF) of a lightweight Fe-30Mn-10Al-1C (in wt.%) alloy after gas nitridation were investigated. The gas nitriding process was performed at 550 degrees C for 5 h under pure NH3 atmosphere. The nitrided layer was similar to 45 mu-thick and consisted predominantly of fine AlN. The surface microhardness, ultimate tensile strength, yield strength, and elongation of the present gas-nitrided alloy are 1814 Hv, 1078 MPa, 1024 MPa, and 77%, respectively. The corrosion tests in SBF showed that the gas-nitrided alloy exhibited a corrosion current density (I-corr) of 5.0 x 10(-9) A/cm(2), a pitting corrosion current density (I-pit) of 5.1 x 10(-7) A/cm(2), and a passivation region with Delta E (equivalent to E-p - E-corr) approximate to + 1804 mV, respectively, which are substantially better than those obtained in the plasma-nitrided and hydroxyapatite-coated 316L stainless steel. The results demonstrated that the present gas-nitrided alloy having an excellent combination of strength, ductility and corrosion resistance is a promising candidate to replace 316L stainless steel for medical implants. (C) 2018 Elsevier B.V. All rights reserved.