Characterizations of GaN Films Grown on Si (111) Substrates with Various Growth Temperatures of Multiple AlN Buffer Layers
(2012)
Binh-Tinh Tran
;
Chang, Edward Yi
;
Lin, Kung-Liang
;
Luong, Tien-Tung
;
Yu, Hung-Wei
We present the effect of multiple AlN buffer layers on characterizations of GaN film quality, which includes a thin high-low-high-temperature (HLHT) AlN buffer layers. The study is based on two different thicknesses of the GaN films on the buffers and found that the HLHT AlN buffer layers could significantly affect on the GaN films qualities. The buffer plays a very important role for the growth of GaN film on Si (111) substrate. The GaN film with an uniformly faceted surface and very high-quality has been obtained at the optimized multiple HLHT AlN buffer layers of 50-nm-thick at 1010-800-1010 degrees C.
Fabrication and characterization of n-In0.4Ga0.6N/p-Si solar cell
(2012-07-01)
Tran, Binh-Tinh
;
Chang, Edward-Yi
;
Trinh, Hai-Dang
;
Lee, Ching-Ting
;
Sahoo, Kartika Chandra
Electro-optic characteristics of a fabricated n-In0.4Ga0.6N/p-Si hetero-structure solar cell on Si substrate with Al and ITO (or Ti/Al/Ni/Au) materials for p and n-type contacts were investigated in this letter. The solar cell devices with ITO as n-type contacts were also compared to the solar cell using Ti/Al/Ni/Au as n-type contact in this study. High short-circuit current density observed for solar cell with ITO as n-type contacts due to the increased amount of light reaching the solar cell. The device with ITO contact exhibited an open-circuit voltage (V-oc) of 1.52 V and a short-circuit current density (J(sc)) of 8.68 mA/cm(2) with 54% fill factor. The conversion and external quantum efficiency (EQE) of the solar cell were 7.12 and 20.8%, respectively. Besides, a relationship between V-oc and In content in the InxGa1-xN alloys for this type of solar cell was also derived. (C) 2012 Elsevier B.V. All rights reserved.
Growth of High-Quality In(0.4)Ga(0.6)N Film on Si Substrate by Metal Organic Chemical Vapor Deposition
(2011-11-01)
Binh-Tinh Tran
;
Chang, Edward-Yi
;
Lin, Kung-Liang
;
Wong, Yuen-Yee
;
Sahoo, Kartika Chandra
High-quality In(0.4)Ga(0.6)N film grown on GaN/AlN/Si(111) templates was obtained by metal organic chemical vapor deposition (MOCVD) with negligible phase separation. A template of high-quality GaN grown on a Si(111) substrate using AlN buffer layers was used for subsequent In(0.4)Ga(0.6)N growth. The GaN layer was 0.6 mu m thick with rocking-curve full width at half maximum (FWHM) for a GaN(002) peak better than 430 arcsec. The In(0.4)Ga(0.6)N film grown was 0.3 mu m thick with a dislocation density of 6 x 10(7) cm(-2) and X-ray (omega-2 theta) FWHM better than 130 arcsec. (C) 2011 The Japan Society of Applied Physics
Growth of High-Quality In0.4Ga0.6N Film on Si Substrate by Metal Organic Chemical Vapor Deposition
(2011-11-01)
Binh-Tinh Tran
;
Chang, Edward-Yi
;
Lin, Kung-Liang
;
Wong, Yuen-Yee
;
Sahoo, Kartika Chandra
High-quality In0.4Ga0.6N film grown on GaN/AlN/Si(111) templates was obtained by metal organic chemical vapor deposition (MOCVD) with negligible phase separation. A template of high-quality GaN grown on a Si(111) substrate using AlN buffer layers was used for subsequent In0.4Ga0.6N growth. The GaN layer was 0.6 mu m thick with rocking-curve full width at half maximum (FWHM) for a GaN(002) peak better than 430 arcsec. The In0.4Ga0.6N film grown was 0.3 mu m thick with a dislocation density of 6 x 10(7) cm(-2) and X-ray (omega-2 theta) FWHM better than 130 arcsec. (C) 2011 The Japan Society of Applied Physics