Efficient inverted quasi-bilayer organic solar cells fabricated by using non-halogenated solvent processes
(2014-09-07)
Chang, Jung-Hao
;
Wang, Hsiao-Fang
;
Lin, Wei-Chieh
;
Chiang, Kai-Ming
;
Chen, Kuan-Chen
Here we demonstrate the fabrication of novel, "quasi-bilayer" inverted organic photovoltaic devices using halogen-free solvents. The inferior solubility of pristine fullerene in non-halogenated solvents was used to control the interpenetration of upper polymeric donor layers with bottom fullerene layers. Notably, island-like nano-morphologies were revealed by AFM, SEM, TEM, cross-sectional TEM images and PL quenching measurement. Correlation between device performance, thin-film nano-morphology and ac impedance was observed. High efficiencies of 6.55% and 7.15% were observed for PBDTTT-C-T and PTB7 cells, respectively. These results demonstrate that this novel process not only offers an effective new method to control the morphology of solar active layers but, more importantly, could also be applied to a wide range of current material systems to produce efficient devices that comply with the non-toxic halogen-free requirement.
Efficient inverted quasi-bilayer organic solar cells fabricated by using non-halogenated solvent processes
(2014-09-07)
Chang, Jung-Hao
;
Wang, Hsiao-Fang
;
Lin, Wei-Chieh
;
Chiang, Kai-Ming
;
Chen, Kuan-Chen
Here we demonstrate the fabrication of novel, "quasi-bilayer" inverted organic photovoltaic devices using halogen-free solvents. The inferior solubility of pristine fullerene in non-halogenated solvents was used to control the interpenetration of upper polymeric donor layers with bottom fullerene layers. Notably, island-like nano-morphologies were revealed by AFM, SEM, TEM, cross-sectional TEM images and PL quenching measurement. Correlation between device performance, thin-film nano-morphology and ac impedance was observed. High efficiencies of 6.55% and 7.15% were observed for PBDTTT-C-T and PTB7 cells, respectively. These results demonstrate that this novel process not only offers an effective new method to control the morphology of solar active layers but, more importantly, could also be applied to a wide range of current material systems to produce efficient devices that comply with the non-toxic halogen-free requirement.
ITO-free inverted polymer solar cell on metal substrate with top-illumination
(2014-01-01)
Chen, En-Chen
;
Tsai, Pei-Ting
;
Tsai, Chia-Ying
;
Chang, Jung-Hao
;
Huang, Zheng-Yu
High-performance polymer solar cells are conventionally fabricated on the rigid and costly indium-tin-oxide (ITO) glass substrates, which are incompatible with the roll-to-roll process with low cost. This study shows that polymer solar cells can be made on ITO-free flexible stainless steel with only a moderate compromise in power conversion efficiency. A blend of poly (3-hexylthiophene) (P3HT) and (6,6)-phenyl-C61-butyric acid methyl ester (PCBM) was used as the active material for the inverted structure. The bottom electrode was an alloy of Al and Au spontaneously formed from a bi-layer during thermal annealing of the active layer. This alloy had a low work function of 3.9 eV, and a high resistance to oxide formation throughout the entire process. Semi-transparent Ag was used as the top electrode. These solar cells on stainless steel had an efficiency of 2.6%. The majority of the loss came from the top electrode transmission at approximately 60%. This all-metal approach makes roll-to-roll polymer cell fabrication possible. (C) 2013 Elsevier B.V. All rights reserved.