Microstructural investigation of oxidized Ni/Au ohmic contact to p-type GaN
(1999-01-01)
Chen, LC
;
Chen, FR
;
Kai, JJ
;
Chang, L
;
Ho, JK
The phase evolution of oxidized (10nm) Ni/(5nm) Au films on p-GaN was examined with a field emission gun transmission electron microscope in conjunction with composition analyses to explore the mechanism of formation of low resistance ohmic contact to p-GaN. The p-GaN/Ni/Au sample heat treated above 500 degreesC in air was mainly composed of a mixture of crystalline NiO, Au and amorphous Ni-Ga-O phases. Small voids adjacent to the p-GaN film were also found. Moreover, NiO partially contacts to p-GaN as well as Au islands and the amorphous Ni-Ga-O phases. The results suggest that the crystalline NiO and/or amorphous Ni-Ga-O phases may play a significant role in the formation of a low resistance ohmic contact to p-GaN.
Microstructural investigation of oxidized Ni/Au ohmic contact to p-type GaN
(1999)
Chen, LC
;
Chen, FR
;
Kai, JJ
;
Chang, L
;
Ho, JK
The microstructure of oxidized Ni/Au films on p-GaN was examined to elucidate the formation of a low resistance ohmic contact to p-GaN with a field-emission gun transmission electron microscope in conjunction with composition analyses. The p-GaN/Ni/Au samples were heat treated at 500 degrees C in air mainly composed of a mixture of crystalline NiO, Au, and amorphous Ni-Ga-O phases. Small voids adjacent to the p-GaN film were also observed. The as-deposited Au film converted into discontinuous islands containing small amounts of Ni that connect with p-GaN. NiO formed a continuous film at the surface that covers the Au islands and the amorphous Ni-Ga-O phases. Moreover, NiO partially contacts p-GaN as well as Au islands and the amorphous Ni-Ga-O phase. The orientation relationship of the crystalline NiO, Au-rich islands, and p-GaN film was identified as NiO(111)//Au(11 (1) over bar)//GaN(0002) and NiO[1 (1) over bar 0]//Au[1 (1) over bar 0]//GaN[11 (2) over bar 0]. The results suggested that Ni atoms diffuse through the Au layer onto the surface and react with oxygen to form NiO, whereas Au atoms diffuse towards the inside to form a Au-Ni alloy. The microstructural examination indicated that the crystalline NiO and/or the amorphous Ni-Ga-O phases may significantly affect the low resistance ohmic contact to p-GaN. (C) 1999 American Institute of Physics. [S0021-8979(99)05219-6].
The effect of heat treatment on Ni/Au ohmic contacts to p-type GaN
(1999-11-16)
Chen, LC
;
Ho, JK
;
Chen, FR
;
Kai, JJ
;
Chang, L
The effect of heat treatment temperature on the microstructure and specific contact resistance of oxidized Ni(5 nm)/Au(5 nm) contacts to p-type GaN was investigated.,The: minimum specific contact resistance (Q(c)) obtained was 4 x 10(-6) Omega cm(2) after heat treating at 500 degrees C in air for 10 min. The cross-sectional microstructure of heat treated Ni/Au films on p-type GaN was examined with transmission electron microscope (TEM) in conjunction with compositional analyses. The high value of Q(c) for samples heat treated at lower temperatures (< 400 degrees C) was attributed to the fact that Au islands and crystalline NiO detached from the p-type GaN. When the temperature increased to 500 degrees C, NiO films and Au islands epitaxially constructed on p-type GaN matrix. The crystalline NiO may play a crucial role in the formation of low-resistance ohmic contact to p-GaN. Increasing the temperature further to 600 degrees C, large voids adjacent to p-GaN were observed which resulted in the reduction of contacting area deteriorating the contact resistance.