Antiferroelectric antiferromagnetic type-I multiferroic Cu9O2(SeO3)(4)Cl-6
(2019-12-11)
Wu, H. C.
;
Denisova, K. N.
;
Menzel, D.
;
Kakarla, D. Chandrasekhar
;
Maximova, O. V.
We report that Cu9O2(SeO3)(4)Cl-6 is a new multiferroic compound. Comprehensive studies of this compound have been carried out on single crystals as well as polycrystalline samples. Magnetic susceptibility chi and specific heat C with H parallel to c axis both reveal an anomaly at T-N = 37 K associated with the long-range antiferromagnetic order. However, no signature of this phase transition is seen with the H parallel to b axis, providing evidence of the anisotropic nature of its magnetic properties. The results of chi measurements are consistent with the temperature evolution of the intensity of magnetic reflections from the neutron diffraction experiments. The magnetic structure derived from neutron scattering measurements shows that half of the Cu(5) ions carry no moments. Furthermore, an anomaly in the dielectric constant near T-N and observable magnetoelectric coupling below T-N are found. At high temperatures, a dielectric peak at T-E = 267 K is identified with no measurable spontaneous polarization below T-E, thereby suggesting an antiferroelectric order. A steplike anomaly seen in chi(T) at T-E hints the weak spin-lattice coupling. Concomitantly, high-resolution temperature-dependent synchrotron x-ray diffraction experiments elucidate a local structural distortion at T-E.
Metamagnetic transitions and magnetoelectric coupling in acentric and nonpolar Pb2MnO4
(2019-05-16)
Kakarla, D. Chandrasekhar
;
Wu, H. C.
;
Hsieh, D. J.
;
Sun, P. J.
;
Dai, G. J.
Acentric and nonpolar Pb2MnO4 was predicted to exhibit unique multipiezo induced magnetoelectric (ME) phenomena. In this paper, we present the results of magnetization as well as dielectric properties as a function of temperature (T), magnetic field (H), pressure (P), and electric field (E) primarily to address the ME coupling and identify the underlying mechanism behind this phenomenon. Magnetization and specific-heat measurements reveal the antiferromagnetic ordering of Mn4+ spins at temperature T-N= 17 K. Metamagnetic transitions at three critical magnetic fields H-c1, H-c2 and H-c3) are observed for T < T-N and H > 3.5 T. Further, the influences of pressure and magnetic field on H-c1 and H-c2 are investigated. The T-N, H-c1, and H(c2)( )all decrease with increasing external pressure. The dielectric anomaly observed at T-N is influenced by applying a magnetic field of H > 3.5 T. However, the electric field has minimal influence on the metamagnetic transition. The scaling between dielectric constant and magnetization meaningfully resolves the existence of magnetic-field-induced higher-order ME coupling in Pb2MnO4 at T < T-N and H > 3.5 T.