Browsing by Author "Ko, CC"

Now showing 1 - 4 of 4

Barrier characteristics of PECVD alpha-SiC : H dielectrics
(2001)
Chiang, CC
;
Wu, ZC
;
Wu, WH
;
Chen, MC
;
Ko, CC
This work investigates the thermal stability and barrier characteristics of three species of PECVD alpha-SiC:H dielectric films with dielectric constants between 3.5 and 5.4. It is found that the dielectric constant decreases with increasing content of carbon in the alpha-SiC:H film. All of the three specie's of alpha-SiC:H films are thermally stable at temperatures of up to 500degreesC. However, degraded barrier capability and moisture resistance were observed for the alpha-SiC:H film with a k value around 3.5, which has a C/Si atomic ratio of 0.875. This is presumably attributed to poorly crosslinked molecular structure and porosity enhancement by the abundant amount of carbon in the alpha-SiC:H film.
Physical and barrier properties of plasma enhanced chemical vapor deposition alpha-SiC : N : H films
(2003-07-01)
Chiang, CC
;
Wu, ZC
;
Wu, WH
;
Chen, MC
;
Ko, CC
In this work, we investigate the thermal stability and physical and barrier properties of three species of plasma enhanced chemical vapor deposition (PECVD) alpha-SiC:N:H silicon carbide films with different carbon and nitrogen contents and dielectric constants less than a value of 5.5. For comparison, one species of alpha-SiN:H film with a k value of 7.2 is also studied. It is found that the dielectric constant decreases with increasing content of carbon and decreasing content of nitrogen in the alpha-SiC:N:H film. All of the three species of alpha-SiC:N:H and the one species of alpha-SiN:H films are thermally stable at temperatures up to 500degreesC. However, degraded barrier capability and moisture resistance were observed for the alpha-SiC:N:H film with a k value of 3.5, which has a C/Si atomic ratio of 0.875. This is presumably due to the poorly crosslinked molecular structure and porosity enhancement caused by the abundant amount of carbon in the alphaSiC:N:H film.
Physical and barrier properties of plasma-enhanced chemical vapor deposited alpha-SiC : H films from trimethylsilane and tetramethylsilane
(2003-07-01)
Chiang, CC
;
Chen, MC
;
Ko, CC
;
Wu, ZC
;
Jang, SM
This work investigates the thermal stability and physical and barrier properties of two species of plasma-enhanced chemical vapor deposited (PECVD) alpha-SiC:H silicon carbide films (with k-values less than 5) deposited using trimethylsilane, (CH3)(3)SiH (3MS) and tetramethylsilane, (CH3)(4)Si (4MS) organosilicate gases. It is found that the 4MS alpha-SiC:H film contains a higher content of carbon and has a lower dielectric constant. Both of the 3MS and 4MS alpha-SiC:H films are thermally stable at temperatures up to 500degreesC. However, degraded barrier property and moisture resistance were observed for the 4MS alpha-SiC:H film; this is attributed to the porosity enrichment caused by the film's high carbon content. The 3MS alpha-SiC:H film, which exhibits a superior Cu-barrier property, is a potential candidate for replacing the higher dielectric constant Si3N4 film as a Cu-cap barrier and etching stop layer in the Cu damascene structure.
Physical and barrier properties of plasma-enhanced chemical vapor deposited alpha-SiCN : H films with different hydrogen contents
(2003-08-01)
Chiang, CC
;
Chen, MC
;
Ko, CC
;
Jang, SM
;
Yu, CH
This work investigates the thermal stability and physical and barrier properties of two species of plasma-enhanced chemical-vapor-deposited (PECVD) amorphous silicon-nitrocarbide (alpha-SiCN:H) films with different hydrogen contents and dielectric constants of less than 5. It is found that the alpha-SiCN:H film with a higher hydrogen content has a lower dielectric constant. Both species of alpha-SiCN:H films are thermally stable at temperatures up to 500degreesC. However, a degraded dielectric strength was observed for the alpha-SiCN:H film with a lower k-value of 4, which has a much higher hydrogen content. This may be attributed to hydrogen-related defects, such as Si-H+-Si hydrogen bridges, and numerous Si-H weak bonds produced by the high hydrogen content in the alpha-SiCN:H film.