Berezinskii-Kosterlitz-Thouless transition in an Al superconducting nanofilm grown on GaAs by molecular beam epitaxy
(2020-05-15)
Su, Guan-Ming
;
Wu, Bi-Yi
;
Fan, Yen-Ting
;
Kumar, Ankit
;
Chang, Chau-Shing
We have performed extensive transport experiments on a 4 nm thick aluminum (Al) superconducting film grown on a GaAs substrate by molecular beam epitaxy (MBE). Nonlinear current-voltage (I-V) measurements on such a MBE-grown superconducting nanofilm show that V similar to I-3, which is evidence for the Berezinskii-Kosterlitz-Thouless (BKT) transition, both in the low-voltage (T-BKT 1.97 K) and high-voltage regions (T-BKT 2.17 K). In order to further study the two regions where the I-V curves are BKT-like, our experimental data are fitted to the temperature-induced vortices/antivortices unbinding model as well as the dynamical scaling theory. It is found that the transition temperature obtained in the high-voltage region is the correct T-BKT as confirmed by fitting the data to the aforementioned models. Our experimental results unequivocally show that I-V measurements alone may not allow one to determine T-BKT for superconducting transition. Therefore, one should try to fit one's results to the temperature-induced vortices/antivortices unbinding model and the dynamical scaling theory to accurately determine T-BKT in a two-dimensional superconductor.
Topological Transition in a 3nm Thick Al Film Grown by Molecular Beam Epitaxy
(2019-12-27)
Kumar, Ankit
;
Su, Guan-Ming
;
Chang, Chau-Shing
;
Yeh, Ching-Chen
;
Wu, Bi-Yi
We have performed detailed transport measurements on a 3nm thick (as-grown) Al film on GaAs prepared by molecular beam epitaxy (MBE). Such an epitaxial film grown on a GaAs substrate shows the Berezinskii-Kosterlitz-Thouless (BKT) transition, a topological transition in two dimensions. Our experimental data shows that the MBE-grown Al nanofilm is an ideal system for probing interesting physical phenomena such as the BKT transition and superconductivity. The increased superconductor transition temperature (similar to 2.4K) compared to that of bulk Al (1.2K), together with the ultrathin film quality, may be advantageous for future superconductor-based quantum devices and quantum information technology.