Enabling Lambertian-Like Warm White Organic Light-Emitting Diodes with a Yellow Phosphor Embedded Flexible Film
(2014-01-01)
Chen, Cheng-Chang
;
Lin, Huang-Yu
;
Li, Cheng-Hung
;
Wu, Jin-Han
;
Tu, Zong-Yi
We demonstrate in this report a new constructive method of fabricating white organic light-emitting devices (OLEDs) with a flexible plastic film embedded with yellow phosphor. The flexible film is composed of polydimethylsiloxane (PDMS) and fabricated by using spin coating followed by peeling technology. From the results, the resultant electroluminescent spectrum shows the white OLED to have chromatic coordinates of 0.38 and 0.54 and correlated color temperature of 4200 K. The warm white OLED exhibits the yield of 10.3 cd/A and the luminous power efficiency of 5.4 lm/W at a luminance of 1000 cd/m(2). A desirable Lambertian-like far-field pattern is detected from the white OLEDs with the yellow phosphor containing PDMS film. This method is simple, reproducible, and cost-effective, proving to be a highly feasible approach to realize white OLED.
Enabling Lambertian-Like Warm White Organic Light-Emitting Diodes with a Yellow Phosphor Embedded Flexible Film
(2014-01-01)
Chen, Cheng-Chang
;
Lin, Huang-Yu
;
Li, Cheng-Hung
;
Wu, Jin-Han
;
Tu, Zong-Yi
We demonstrate in this report a new constructive method of fabricating white organic light-emitting devices (OLEDs) with a flexible plastic film embedded with yellow phosphor. The flexible film is composed of polydimethylsiloxane (PDMS) and fabricated by using spin coating followed by peeling technology. From the results, the resultant electroluminescent spectrum shows the white OLED to have chromatic coordinates of 0.38 and 0.54 and correlated color temperature of 4200 K. The warm white OLED exhibits the yield of 10.3 cd/A and the luminous power efficiency of 5.4 lm/W at a luminance of 1000 cd/m(2). A desirable Lambertian-like far-field pattern is detected from the white OLEDs with the yellow phosphor containing PDMS film. This method is simple, reproducible, and cost-effective, proving to be a highly feasible approach to realize white OLED.
Large-area ultraviolet GaN-based photonic quasicrystal laser with high-efficiency green color emission of semipolar {10-11} In0.3Ga0.7N/GaN multiple quantum wells
(2013-01-07)
Chen, Cheng-Chang
;
Chiu, Ching-Hsueh
;
Chang, Shih-Pang
;
Shih, M. H.
;
Kuo, Ming-Yen
In this study, a multi-color emission was observed from the large-area GaN-based photonic quasicrystal (PQC) nanopillar laser. The GaN PQC nanostructure was fabricated on an n-GaN layer by using nanoimprint lithographic technology. The regrown InGaN/GaN multiple quantum wells (MQWs) formed a nanopyramid structure on top of the PQC nanopillars. A lasing action was observed at ultraviolet wavelengths with a low threshold power density of 24 mJ/cm(2), and a green color emission from InGaN/GaN MQWs was also achieved simultaneously. (C) 2013 American Institute of Physics. [http://dx.doi.org/10.1063/1.4775373]