Ca(2)PO(4)Cl : Eu(2+): an intense near-ultraviolet converting blue phosphor for white light-emitting diodes
(2010-01-01)
Chiu, Yi-Chen
;
Liu, Wei-Ren
;
Chang, Chun-Kuei
;
Liao, Cheng-Chun
;
Yeh, Yao-Tsung
A blue phosphor Ca(2)PO(4)Cl : Eu(2+) was synthesized by solid state reaction and evaluated as a candidate for white LEDs. The luminescent intensity of Ca(2)PO(4)Cl : Eu(2+) was found to be 128% under excitation at 380 nm, 149% under 400 nm, and 247% under 420 nm, as high as that of BaMgAl(10)O(17) : Eu(2+). Furthermore, Ca(2)PO(4)Cl : Eu(2+) reveals high quantum efficiency and excellent thermal stability. By utilizing a mixture of blue-emitting Ca(2)PO(4)Cl : Eu(2+), green-emitting (Ba, Sr)(2)SiO(4) : Eu(2+) and redemitting CaAlSiN(3) : Eu(2+) as light converters, an intense white GaN-based n-UV-LED (400 nm) was fabricated to exhibit an excellent color-rendering index R(a) of 93.4 at a correlated color temperature of 4590 K. Based on the results, we are currently evaluating the potential application of Ca(2)PO(4)Cl : Eu(2+) as a blue-emitting near-UV convertible phosphor.
Ca2PO4Cl : Eu2+: an intense near-ultraviolet converting blue phosphor for white light-emitting diodes
(2010-01-01)
Chiu, Yi-Chen
;
Liu, Wei-Ren
;
Chang, Chun-Kuei
;
Liao, Cheng-Chun
;
Yeh, Yao-Tsung
A blue phosphor Ca2PO4Cl : Eu2+ was synthesized by solid state reaction and evaluated as a candidate for white LEDs. The luminescent intensity of Ca2PO4Cl : Eu2+ was found to be 128% under excitation at 380 nm, 149% under 400 nm, and 247% under 420 nm, as high as that of BaMgAl10O17 : Eu2+. Furthermore, Ca2PO4Cl : Eu2+ reveals high quantum efficiency and excellent thermal stability. By utilizing a mixture of blue-emitting Ca2PO4Cl : Eu2+, green-emitting (Ba, Sr)(2)SiO4 : Eu2+ and redemitting CaAlSiN3 : Eu2+ as light converters, an intense white GaN-based n-UV-LED (400 nm) was fabricated to exhibit an excellent color-rendering index R-a of 93.4 at a correlated color temperature of 4590 K. Based on the results, we are currently evaluating the potential application of Ca2PO4Cl : Eu2+ as a blue-emitting near-UV convertible phosphor.
Intense blue-emitting Ca(2)PO(4)Cl:Eu(2+) phosphor for near-ultraviolet converting white light-emitting diodes
(2010-12-01)
Chiu, Yi-Chen
;
Liu, Wei-Ren
;
Chang, Chun-Kuei
;
Liao, Cheng-Chun
;
Yeh, Yao-Tsung
A blue phosphor Ca(2)PO(4)Cl:Eu(2+) (CAP:Eu(2+)) was synthesized by solid state reaction. The Ca(2)PO(4)Cl:Eu(2+) exhibited high quantum efficiency and excellent thermal stability. The luminescent intensity of Ca(2)PO(4)Cl:Eu(2+) was found to be 128% under excitation at 380 nm, 149% under 400 nm, and 247% under 420 nm as high as that of BaMgAl(10)O(17):Eu(2+). The optimal doping concentration was observed to 11 mol.% of CAP:Eu(2+). The energy transfer between Eu(2+) ions in CAP were occurred via electric multipolar interaction, and the critical transfer distance was estimated to be 1.26 nm. A mixture of blue-emitting Ca(2)PO(4)Cl:Eu(2+), green-emitting (Ba,Sr)(2)SiO(4):Eu(2+) and red-emitting CaAlSiN(3):Eu(2+) phosphors were selected in conjunction with 400 nm chip to fabricate white LED devices. The average color-rendering index R(a) and correlated color temperature (T(c)) of the white LEDs were found to be 93.4 and 4590 K, respectively. The results indicated that it was a promising candidate as a blue-emitting phosphor for the near-UV white light-emitting diodes.
Intense blue-emitting Ca2PO4Cl:Eu2+ phosphor for near-ultraviolet converting white light-emitting diodes
(2010-12-01)
Chiu, Yi-Chen
;
Liu, Wei-Ren
;
Chang, Chun-Kuei
;
Liao, Cheng-Chun
;
Yeh, Yao-Tsung
A blue phosphor Ca2PO4Cl:Eu2+ (CAP:Eu2+) was synthesized by solid state reaction. The Ca2PO4Cl:Eu2+ exhibited high quantum efficiency and excellent thermal stability. The luminescent intensity of Ca2PO4Cl:Eu2+ was found to be 128% under excitation at 380 nm, 149% under 400 nm, and 247% under 420 nm as high as that of BaMgAl10O17:Eu2+. The optimal doping concentration was observed to 11 mol.% of CAP:Eu2+. The energy transfer between Eu2+ ions in CAP were occurred via electric multipolar interaction, and the critical transfer distance was estimated to be 1.26 nm. A mixture of blue-emitting Ca2PO4Cl:Eu2+, green-emitting (Ba,Sr)(2)SiO4:Eu2+ and red-emitting CaAlSiN3:Eu2+ phosphors were selected in conjunction with 400 nm chip to fabricate white LED devices. The average color-rendering index R-a and correlated color temperature (T-c) of the white LEDs were found to be 93.4 and 4590 K, respectively. The results indicated that it was a promising candidate as a blue-emitting phosphor for the near-UV white light-emitting diodes.