Highly efficient and stable organic solar cell modules processed by blade coating with 5.6% module efficiency and active area of 216 cm(2)
(2019-03-01)
Huang, Kuan-Min
;
Wong, Ying Qian
;
Lin, Man-Chun
;
Chen, Chao-Hsuan
;
Liao, Chung-Hung
In this study, an efficient and stable large-area blade-coated organic solar cell (OSC) module with an active area of 216 cm(2) (16 elementary cells connected in series) is demonstrated by combining appropriate thermal annealing treatment with the use of 4,4 '-(((methyl(4-sulphonatobutyl)ammonio)bis(propane-3,1-diyl))bis(dimethyl-ammoniumdiyl))bis-(butane-1-sulfonate) (MSAPBS) as the cathode interfacial layer. For the opaque device using poly[4,8-bis(5-(2-ethylhexyl)thiophen-2-yl)benzo[1,2-b;4,5-b ']dithiophene-2,6-diyl-alt-(4-(2-ethylhexyl)-3-fluorothieno[3,4-b]thiophene-)-2-carboxylate-2-6-diyl)] (PBDTTT-EFT (PTB7-Th)):[6,6]-phenyl C-71-butyric acid methyl ester (PC71BM) blend film as the active layer, the power conversion efficiency (PCE) of 5.6% is achieved under AM 1.5G solar light illumination. Very encouragingly, our strategy can be applicable for semitransparent OSCs, and a remarkable PCE up to 4.5% is observed. To the best of our knowledge, the PCE of 5.6% for opaque device and 4.5% for semitransparent device represent the highest PCE ever reported for OSCs with the active area exceeding 100 cm(2). The devices also show an impressive stability under outdoor environment, where the efficiency decay is less than 30% for 60 days. Our findings can pave the way toward the development of organic solar cell modules with high performance and long-term stability.
Large-area blade-coated organic solar cells processed from halogen-free solvent
(2019-12-01)
Chen, Szu-Han
;
Liao, Chung-Hung
;
Chang, Chih-Yu
;
Huang, Kuan-Min
;
Chen, Jen-Yueh
High performance organic solar cells (OSCs) are generally prepared by halogenated solvents, which are detrimental to the environment and human health. The replacement of hazardous halogenated solvents is a priority in the commercialization of solution-processed OSCs. In this study, poly[4,8-bis(5-(2-ethylhexyl)thiophen-2-yl) benzo [1,2-b;4,5-b'] dithiophene-2,6-diyl-alt-(4- (2-ethylhexyl)-3-fluorothieno [3,4-b] thiophene-)-2-carboxylate-2-6-diyl)] (PBDTTT-EFT):[6,6]-phenyl C-71 -butyric acid methyl ester (PC71BM)-based device processed with binary halogen-free solvents (toluene and N-methyl-2-pyrrolidone) is fabricated by blade-coating method. Through the combination of morphological manipulation of active layer and interfacial engineering, the resulting OSCs deliver a promising power conversion efficiency (PCE) up to 11.09%. Importantly, large-area (216 cm(2)) blade-coated bulk-heterojunction OSCs is also demonstrated, and the resulting devices deliver a high PCE up to 5.03%, which is comparable to those of the devices processed with halogenated solvents (PCE = 5.20%). Additionally, the devices processed with halogen-free solvents also exhibit superior stability, maintaining 88% of its initial efficiency after 3960 h of continuous operation. More encouragingly, halogen-free solvents-based manufacturing process can also be performed under ambient conditions, and a moderate PCE of 3.67% is attained for large-area (216 cm(2)) OSCs. To the best of our knowledge, 3.67% represents the highest efficiency ever reported for air-processed large-area OSCs. This work paves the way towards the realization of environmentally-friendly large-area OSCs with high performance and long-term stability.
Toward Long-Term Stable and Efficient Large-Area Organic Solar Cells
(2017-07-10)
Tsai, Pei-Ting
;
Lin, Kuan-Chu
;
Wu, Cheng-Yu
;
Liao, Chung-Hung
;
Lin, Man-Chun
Here, we report that long-term stable and efficient organic solar cells (OSCs) can be obtained through the following strategies: i) combination of rapid-drying blade-coating deposition with an appropriate thermal annealing treatment to obtain an optimized morphology of the active layer; ii) insertion of interfacial layers to optimize the interfacial properties. The resulting devices based on poly[4,8-bis(5-(2-ethylhexyl)thiophen-2-yl)-benzo[1,2-b;4,5-b']dithiophene-2,6-diyl-alt-(4-(2-ethylhexyl)-3-fluorothieno[3,4-b]thiophene-2-carboxylate-2,6-diyl)] (PBDTTT-EFT):[6,6]-phenyl C-71 butyric acid methyl ester (PC71BM) blend as the active layer exhibits a power conversion efficiency (PCE) up to 9.57 %, which represents the highest efficiency ever reported for blade-coated OSCs. Importantly, the conventional structure devices based on poly(3-hexylthiophene) (P3HT):phenyl-C-61-butyric acid methyl ester (PCBM) blend can retain approximately 65% of their initial PCE for almost 2 years under operating conditions, which is the best result ever reported for long-term stable OSCs under operational conditions. More encouragingly, long-term stable large-area OSCs (active area = 216 cm(2)) based on P3HT:PCBM blend are also demonstrated. Our findings represent an important step toward the development of large-area OSCs with high performance and long-term stability.