Investigating Material Changes at Different Gadolinium Doping Power Levels in Indium-Tin Oxide Intended for Use as an Insulator in Resistive Switching Memory
(2019-06-01)
Lin, Chun-Chu
;
Chen, Po-Hsun
;
Chen, Min-Chen
;
Chang, Ting-Chang
;
Lin, Chih-Yang
This paper investigates material modifications induced by cosputtering indium-tin oxide (ITO) with gadolinium (Gd) at two different power levels. In addition, resistance switching (RS) properties were also verified for use as an insulator in resistive random access memory (RRAM). Comparison of scanning electron microscope (SEM) measurements for the two different cosputtering powers indicated significant changes of the ITO surface. Transparency was also verified by an N&K analyzer measurement, with results indicating a constant in transparency induced by the lower power Gd doping, indicating potential for transparent applications. Furthermore, the mole fraction ratio defined by X-ray photoelectron spectroscopy reveals a Gd2O3 peak, a likely reason for the ITO thin film becoming less conductive. This ITO/Gd:ITO/TiN RRAM can exhibit stable and robust RS characteristics at a lower forming voltage. In addition, lower operating voltages, including both SET and RESET voltages, can be obtained. Reliability tests including endurance and retention were carried out to confirm its RS stability. The RS mechanism of this ITO/Gd:ITO/TiN device was also investigated with the current-voltage (I-V) fitting method. Moreover, temperature effects were also applied to verify the high-resistance state (HRS) mechanism. Finally, a conduction model was proposed to clarify the RS characteristics and confirm that the ITO/Gd:ITO/TiN device is appropriate for data storage.
The Demonstration of Increased Selectivity During Experimental Measurement in Filament-Type Vanadium Oxide-Based Selector
(2018-10-01)
Chen, Chun-Kuei
;
Lin, Chih-Yang
;
Chen, Po-Hsun
;
Chang, Ting-Chang
;
Shih, Chih-Cheng
In this paper, vanadium oxide (VOx) was chosen for the resistive switching layer in a typical resistive random access memory (PRAM) structure. During negative forming bias, we found an initial selector property. This indicates the presence of metal-insulator-transition characteristics in the VOx layer even without an annealing process. In order to study this phenomenon, material analyses were conducted, with results indicating that there are V-O stretching bonds and an oxide/vanadium ratio of nearly 2.2 (O/V. 2.2). In addition, the experimental results of the dc sweeping test indicated that off-state current gradually decreased after each cycle, meaning that the selectivity characteristics in the VOx selector could be improved. Endurance performance of our experimental devices reached 10(8), sufficient for integration with RRAM devices in a 1S1R array. To further investigate this special phenomenon, current fitting analysis and simulation analyses were conducted. The results of the fitting analysis indicated that the conduction mechanism for off-state current was Schottky emission and the Schottky distance increased with increasing numbers of cycles. In other words, oxide ions migrate toward the filament at low negative voltage during dc sweeping, causing the formation of VOx. Furthermore, the results of thermal field simulation analysis indicated that there is a thermal concentration effect in and around the filament. Thus, oxide ions more easily migrate toward the vanadium filament when a stronger electrical field is present around the filament during dc sweeping cycles. Finally, stable vanadium selector characteristics are obtained and a conduction filament behavior model is proposed.
The influence of temperature on set voltage for different high resistance state in 1T1R devices
(2019-02-01)
Tan, Yung-Fang
;
Su, Yu-Ting
;
Chen, Min-Chen
;
Chang, Ting-Chang
;
Tsai, Tsung-Ming
HfO2-based 1T1R is researched in this paper. The on-off ratio is an important electrical characteristic of RRAM, with a larger on-off ratio being preferable. However, temperature also affects the set process when operating RRAM. This study finds that the set process has different sensitivities to temperature at different high resistance states (HRSs). The set voltage of the higher HRS decreases with increasing temperature, while in the lower HRS, set voltage is independent of temperature. From the result, the lower HRS is better for RRAM because it is stable at different temperatures. (C) 2019 The Japan Society of Applied Physics