Fabrication and Characterization of High-k Dielectric Nickel Titanate Thin Films Using a Modified Sol-Gel Method
(2011-01-01)
Chuang, Shiow-Huey
;
Hsieh, Min-Lung
;
Wu, Shih-Chieh
;
Lin, Hong-Cai
;
Chao, Tien-Sheng
This research produced high-quality, single-phase nickel titanate (NiTiO(3)) thin films, a high-k material for gate dielectrics, by a modified sol-gel method. The precursor was prepared by reactions of nickel acetate tetrahydrate and titanium isopropoxide in 2-methoxyethanol with a 1:1 ratio of Ni/Ti in the solution. After coating, the films were post-heat treated between 500 degrees and 900 degrees C. X-ray diffraction indicated that the films deposited at and above 600 degrees C were single-phase nickel titanate. X-ray photoelectron spectra of a typical thin film revealed that the binding energies of Ni 2p(3/2) and Ti 2p(3/2) electrons were 855.2 and 457.7 eV, respectively. Raman spectra showed eight absorptions between 200 and 800 cm-1. Scanning electron microscope images showed smooth surfaces. Findings showed the dielectric constant of the NiTiO(3) film to be 41.36 by capacitance-voltage analysis. The results show that single-phase NiTiO(3) film can be prepared by the sol-gel spin coating method and then heat-treated at 600 degrees C.