Fundamental study on hydration of cement and cement minerals with steam
(1998-01-01)
Lin, WM
;
Lin, TD
;
Hwang, CL
;
Peng, YN
;
土木工程學系
This paper-discusses the basic concept of steam hydration and presents test data oil heat of hydration by exposing cement compounds to pressurized steam. The lest samples include cement and its individual compounds; tricalcium silicate (C3S), dicalcium silicate (C2S), tricalcium aluminate (C(3)A), and tetracalcium aluminoferrite (C(4)AF). For a compacted 10 grams C3S sample, the heat of hydration was determined as 209 cal/g. All samples except C;A hardened during steaming. Nonetheless, rite C(3)A samples reacted very rapidly with steam and registered a 91 C temperature rise during the test. This paper also discusses effects of sample's fineness and degree of compaction on heat evolution and hydrate morphology during exposure to steam. The test results verify the validity of the dry-mix/steam-injection (DMSI) concept.
Microstructures of fire-damaged concrete
(1996-05-01)
Lin, WM
;
Lin, TD
;
PowersCouche, LJ
;
土木工程學系
;
Department of Civil Engineering
This paper presents results of scanning electron microscopy (SEM) and stereo microscopy investigations of fire-damaged concrete. Samples were either taken from concrete that was subjected to heating and cooling of controlled temperatures in the laboratory or removed from concrete and masonry units exposed to fires in the field. By compiling SEM photographs, a clear chronological pattern of a failure mechanism can be visualized. For instance, the morphologies of hydrates from room temperature up to 900 C and reformation of calcium hydroxides (CH) during cooling all have distinguished morphological appearances of their own. Such visual information that would otherwise be impossible to see with the naked eye will help scientists and engineers understand concrete behaviors in fire. This study has focused on microstructures of cement pastes/aggregates, microvoids/cracks, and separation of the cement paste from aggregates in heated concrete samples. An application of lincrete, a type of polyester-polymer concrete developed at National Chiao Tung University, is included to demonstrate the use of a cement-based polymer mortar in the rehabilitation process of fire-damaged concrete.
Microstructures of fire-damaged concrete
(1996-05-01)
Lin, WM
;
Lin, TD
;
PowersCouche, LJ
;
土木工程學系
;
Department of Civil Engineering
This paper presents results of scanning electron microscopy (SEM) and stereo microscopy investigations of fire-damaged concrete. Samples were either taken from concrete that was subjected to heating and cooling of controlled temperatures in the laboratory or removed from concrete and masonry units exposed to fires in the field. By compiling SEM photographs, a clear chronological pattern of a failure mechanism can be visualized. For instance, the morphologies of hydrates from room temperature up to 900 C and reformation of calcium hydroxides (CH) during cooling all have distinguished morphological appearances of their own. Such visual information that would otherwise be impossible to see with the naked eye will help scientists and engineers understand concrete behaviors in fire. This study has focused on microstructures of cement pastes/aggregates, microvoids/cracks, and separation of the cement paste from aggregates in heated concrete samples. An application of lincrete, a type of polyester-polymer concrete developed at National Chiao Tung University, is included to demonstrate the use of a cement-based polymer mortar in the rehabilitation process of fire-damaged concrete.