Facile Synthesis of Diamino-Modified Graphene/Polyaniline Semi-Interpenetrating Networks with Practical High Thermoelectric Performance
(2018-02-07)
Lin, Yen-Hao
;
Lee, Tsung-Chi
;
Hsiao, Yu-Sheng
;
Ling, Wei-Keng
;
Whang, Wha-Tzong
p-Phenediamino-modified graphene (PDG) has been newly synthesized via a facile green one-step chemical route as a functionalized graphene-based additive to copolymerize with aniline for fabricating innovative PDG/polyaniline conducting polymer composites containing very special semi-interpenetrating networks (S-IPNs). The S-IPNs not only provide additional pathways by creating chemically bonded PDG and PANI for smoothly transporting carriers but greatly reduce the amount of graphene required to less than a few percent could effectively improve the overall electrical conductivity, Seebeck coefficient, and thus the thermoelectric (TE) performance. The found optimized TE figure of merit (ZT) of 0.74 approaches a practical high level which is comparable or much higher than previously reported ones for TE polymers.
Humidity-switch chromism of aniline-pentamer in Nafion
(2016-08-19)
Lin, Yen-Hao
;
Hsiao, Yu-Sheng
;
Lu, Hsiao-Chi
;
Chen, Peilin
;
Whang, Wha-Tzong
Aniline-pentamer (AP) in Nafion triggered with humidity content displays an interesting chromism from blue to pink, which is much wider of color shift than general polyaniline. Thermogravimetric analysis confirms the reversal color change related to the moisture content in the sample. IR absorption spectra make known AP having high degree of protonation at lower water content. UV-Vis absorption expose the chromism process having something more than just protonation. The change of electronic energy levels and PL spectra reveal that there must be a complex interaction in NaAP. Raman scattering mapping confirms that drying causes the - SO3- hydrophilic channels transforming to isolated domains dispersed in matrix, which induces heavy protonation and complexation of AP with - SO3- groups. We can infer that the interesting humidity-switch chromism is due to the reversible protonation/deprotonation as well as complexation of AP with - SO3- groups through the reversible change of Nafion\'s morphology.
Particle chain display - an optofluidic electronic paper
(2012-11-21)
Fan, Shih-Kang
;
Chiu, Cheng-Pu
;
Hsu, Ching-Hsiang
;
Chen, Shih-Chiang
;
Huang, Li-Lin
A particle-based display medium and a driving mechanism insensitive to the charge polarity of those particles, based on the transformation of particle chains, are developed for reflective electronic paper displays. Particle chains are formed by dipole-dipole interactions between polarized particles with an appropriate electric field applied across the tested display medium, L e. the solution that regulates the light in the field of display technology, containing neutral polystyrene (PS) particles dispersed in water. Formation of the particle chains results in a large change in optical transmittance and reflectance of the display medium. The performance of the particle chain displays (PCD) was evaluated according to macroscopic (device), microscopic (particle) and optical (reflectance) points of view. A display medium (thickness 100 mu m) containing colored PS particles (3 mu m, 2.5% w/v) was polarized to display the fixed images of the directly driven electrodes and programmable images of arrayed (5 x 5) electrodes with electric fields (0.48 MV m(-1) and 0.09 MV m(-1), 500 kHz, respectively). The formation of particle chains under electric fields (0.2 MV m(-1) and 0.4 MV m(-1), 500 kHz) was observed in the microscopic images of a display medium (thickness 100 mu m) with fluorescent PS particles (5 mu m, 1%). Images recorded with a confocal microscope demonstrated the particle chains. The opacity, a common parameter serving to characterize a display medium, was derived by measuring the reflectance ratio of a black background to a white background of the display medium with varied thickness and particle concentration. The temporal response of a display medium (thickness 50 mu m) with black PS particles (3 mu m, 5%) was tested. When an electric field (0.6 MV m(-1), 500 kHz) was applied, the reflectance increased twice at the first data point in 0.7 s, attaining a contrast ratio of 2. Application of a voltage (20 s) yielded a contrast ratio of 10. The performance of a tested display medium, composed of simple PS particles and water and driven to form particle chains by polarization, is reported.