Fabrication and optoelectronic properties of core-shell biomimetic ZnO/Si nanoball arrays
(2012)
Chang, Yuan-Ming
;
Kao, Pin-Hsu
;
Liu, Mao-Chen
;
Lin, Chih-Ming
;
Lee, Hsin-Yi
We report an effective process scheme comprising a single-step Ag sputtering with subsequent dry etching and atomic layer deposition (ALD) process for fabricating biomimetic ZnO/Si nanoball (ZnO/Si-NB) core-shell nanostructures directly on Si substrates. The obtained ZnO/Si-NB core-shell nanostructures consist of similar to 30 nm thick ZnO films grown on Si frustums produced by means of dry etching masked by the self-assembled silver nanodots created by single-step sputtering. The ZnO films were deposited using atomic layer deposition under an ambient temperature of 200 degrees C. The photoluminescence (PL) measurements on these ZnO/Si-NB core-shell nanostructures showed that the visible range emission was almost completely absent and only the ultraviolet emission (3.28 eV peak) resulting from the free excitons was observed, indicating that the films indeed have high crystalline quality. Moreover, a dramatic improvement of the field emission performance was observed for ZnO/Si-NB core-shell nanostructures as compared to the bare Si frustum arrays. The detailed analyses on the field enhancement factor (beta value) based on the Fowler-Nordheim field emission model indicate that the effective work function of the ZnO/Si-NB core-shell nanostructures might be significantly different from that of either ZnO or Si.
Field Emission in Vertically Aligned ZnO/Si-Nanopillars with Ultra Low Turn-On Field
(2012-03-01)
Chang, Yuan-Ming
;
Liu, Mao-Chen
;
Kao, Pin-Hsu
;
Lin, Chih-Ming
;
Lee, Hsin-Yi
An effective method of fabricating vertically aligned silicon nanopillars (Si-NPs) was realized by using the self-assembled silver (Ag) nanodots as natural metal-nanomask during dry etching process. The obtained Si-NPs were preferentially aligned along the c-axis direction. Ultrathin ZnO films (similar to 9 nm) were subsequently deposited on the Si-NPs by atomic layer deposition (ALD) to enhance the field emission property. The average diameter of the ZnO/Si-NPs is in the order of tens of nanometers, which enables efficient field emission and gives rise to marked improvement in the field enhancement factor, beta. The turn-on field defined by the 10 mu A/cm(2) current density criterion is similar to 0.74 V/mu m with an estimated beta approximate to 1.33x10(4). The low turn-on field and marked enhancement in beta were attributed to the small radius of curvature, high aspect ratio, and perhaps more importantly, proper density distribution of the ZnO/Si-NPs.