Cathodic plasma-induced syntheses of graphene nanosheet/MnO2/WO3 architectures and their use in supercapacitors
(2020-05-10)
Huang, Shih-Yu
;
Phuoc-Anh Le
;
Yen, Po-Jen
;
Lu, Yi-Chun
;
Sahoo, Sumanta Kumar
In this study, we synthesized new 0.01-2 mu m graphene nanosheet/MnO2WO3(G/MnO2/WO3) architectures through an electrochemically induced cathodic plasma process in a single batch at a lower temperature (70 degrees C) and for a shorter time (2 h) than those required for the syntheses of similar structures when using a hydrothermal method. We first obtained 0.01-1 mu m leaf-like graphene (G) nanosheets, then 0.1-0.3 mu m long and approximately 10 nm diameter petiole-like MnO2 nanowires on the G nanosheets, and finally 0.20-2.0 mu m petal-like WO3 on MnO2/G - thereby forming the G/MnO2/WO3 architectures - as evidenced using scanning electron microscopy and transmission electron microscopy. We deciphered the step-wise reaction mechanism behind the formation of the G/MnO2/WO3 architectures during the plasma process. The high surface area of 291 m(2) g(-1) in the G/MnO2/WO3 architecture was contributed mainly by the G nanosheets, providing a suitable surface area for diffusion of the charge carriers during the charging and discharging process. As a result, an electrode incorporating the G/MnO2/WO3 architectures exhibited an excellent specific capacitance of 620 F g(-1) - 45 and 200% higher than those of G/MnO2 (421 F g(-1)) and G (189 F g(-1)) electrodes, respectively - at a current density of 0.5 A g(-1). Moreover, the G/MnO2/WO3-incorporated electrode exhibited good electrochemical cycling stability, with 90% capacitance retention over 5000 cycles at 1 A g(-1). Such new G/MnO2/WO3 heterojunction structures, not only provide high-performance electrode applications, but also suggest a potential approach toward fabricating other heterojunction structures having high surface areas for energy storage applications. (C) 2020 Elsevier Ltd. All rights reserved.
Self-assembly of hierarchical MoSx/CNT nanocomposites (2 < x < 3): towards high performance anode materials for lithium ion batteries
(2013-07-09)
Shi, Yumeng
;
Wang, Ye
;
Wong, Jen It
;
Tan, Alex Yuan Sheng
;
Hsu, Chang-Lung
Two dimension (2D) layered molybdenum disulfide (MoS2) has emerged as a promising candidate for the anode material in lithium ion batteries (LIBs). Herein, 2D MoSx (2 <= x <= 3) nanosheet-coated 1D multiwall carbon nanotubes (MWNTs) nanocomposites with hierarchical architecture were synthesized via a high-throughput solvent thermal method under low temperature at 2006 degrees C. The unique hierarchical nanostructures with MWNTs backbone and nanosheets of MoSx have significantly promoted the electrode performance in LIBs. Every single MoSx nanosheet interconnect to MWNTs centers with maximized exposed electrochemical active sites, which significantly enhance ion diffusion efficiency and accommodate volume expansion during the electrochemical reaction. A remarkably high specific capacity (i.e., >1000 mAh/g) was achieved at the current density of 50 mA g(-1), which is much higher than theoretical numbers for either MWNTs or MoS2 along (similar to 372 and similar to 670 mAh/g, respectively). We anticipate 2D nanosheets/1D MWNTs nanocomposites will be promising materials in new generation practical LIBs.
Self-assembly of hierarchical MoSx/CNT nanocomposites (2<x<3): towards high performance anode materials for lithium ion batteries
(2013-07-09)
Shi, Yumeng
;
Wang, Ye
;
Wong, Jen It
;
Tan, Alex Yuan Sheng
;
Hsu, Chang-Lung
Two dimension (2D) layered molybdenum disulfide (MoS2) has emerged as a promising candidate for the anode material in lithium ion batteries (LIBs). Herein, 2D MoSx (2 <= x <= 3) nanosheet-coated 1D multiwall carbon nanotubes (MWNTs) nanocomposites with hierarchical architecture were synthesized via a high-throughput solvent thermal method under low temperature at 2006 degrees C. The unique hierarchical nanostructures with MWNTs backbone and nanosheets of MoSx have significantly promoted the electrode performance in LIBs. Every single MoSx nanosheet interconnect to MWNTs centers with maximized exposed electrochemical active sites, which significantly enhance ion diffusion efficiency and accommodate volume expansion during the electrochemical reaction. A remarkably high specific capacity (i.e., >1000 mAh/g) was achieved at the current density of 50 mA g(-1), which is much higher than theoretical numbers for either MWNTs or MoS2 along (similar to 372 and similar to 670 mAh/g, respectively). We anticipate 2D nanosheets/1D MWNTs nanocomposites will be promising materials in new generation practical LIBs.