General application of blade coating to small-molecule hosts for organic light-emitting diode
(2014-10-01)
Chang, Hao-Wen
;
Lee, Yi-Ting
;
Tseng, Mei-Rurng
;
Jang, Meng-Hao
;
Yeh, Han-Cheng
Blade coating is applied to multi-layer phosphorescent OLED with five small-molecule hosts for the emission layer, including bis[3,5-di (9H-carbazol-9-yl)phenyl]diphenylsilane (SimCP2), 2,6-bis(3-(9H-carbazol-9-yl)phenyl) pyridine (26DCzPPy), 4,4\',4 \'\'-tris-(N-carbazolyl)-triphenylamine (TCTA), 9,9-bis[4-(3,6-di-tert-butylcarbazol-9-yl)phenyl]fluorene (TBCPF), and 2,7-bis(diphenylphosphoryl)-9,9\'-spirobi[fluorene] (SPPO13). In general, blade coating gives low surface roughness around 0.2 nm without phase separation of the emitter and the host. In the large area of 2 cm by 3 cm the film thickness distribution is within 10% and uniform light-emission is achieved. 1,3-Bis[2-(4-tert-butylphenyl)-1,3,4-oxadiazo-5-yl]benzene (OXD-7) is added to tune the electron transport. Among all the hosts, 26DCzPPy and SimCP2 have by far the best electron hole balance and consequently show the highest efficiency. For SimCP2, the maximal efficiency is 15.8 cd/A for blue and 24.2 cd/A for white emission. The order of efficiencies for the hosts is found to be quite different from the order in vacuum evaporation for the same device structures. (C) 2014 Elsevier B.V. All rights reserved.
Vacuum-free lamination of low work function cathode for efficient solution-processed organic light-emitting diodes
(2012-03-01)
Chang, Yu-Fan
;
Chen, Chun-Yu
;
Luo, Fang-Tsai
;
Chao, Yu-Chiang
;
Meng, Hsin-Fei
The low work function cathode of blade-coated organic light-emitting diode is transferred from a soft polydimethylsiloxane (PDMS) mold by lamination without vacuum. The cathode is a bilayer of polyethylene glycol (PEG) (< 10 nm) and Al (100 nm). A sacrificial layer of polystyrene with low Mw 1500 and melting point of 120 degrees C is inserted between the cathode and PDMS for the subsequent mold removal at 150 degrees C by melting polystyrene. Current efficiency of 3 cd/A (1.1%) and luminance of 2500 cd/m(2) are achieved for green polyfluorene fluorescent emitter. 25 cd/A (8.2%) and 3200 cd/m(2) are achieved for green phosphorescent tris[2-(p-tolyl) pyridine] iridium(III) (Ir(mppy)(3)) emitter in polymer blend host. The efficiency is about 70% of the devices with thermally evaporated cathode. The turn-on voltage is about 5 V higher. (C) 2011 Elsevier B. V. All rights reserved.