Characteristics of the epitaxy of InGaN-based light-emitting diodes grown by nanoscale epitaxial lateral overgrowth using a nitrided titanium buffer layer
(2015-05-01)
Shieh, Chen-Yu
;
Li, Zhen-Yu
;
Chang, Jenq-Yang
;
Chi, Gou-Chung
;
光電工程學系
In this work, a buffer layer of nitrided titanium (Ti) achieved through the nitridation of a Ti metal layer on a sapphire substrate was used for the epitaxial growth of InGaN-based light-emitting diodes (LEDs) achieved by low pressure metal-organic chemical vapor deposition. The effect of in-situ Ti metal nitridation on the performance of these InGaN-based LEDs was then investigated. It was very clear that the use of the nitrided Ti buffer layer (NTBL) induced the formation of a nanoscale epitaxial lateral overgrowth layer during the epitaxial growth. When evaluated by Raman spectroscopy, this epi-layer exhibited large in-plane compressive stress releasing with a Raman shift value of 567.9 cm(-1). Cathodoluminescence spectroscopy and transmission electron microscopy results indicated that the InGaN-based LEDs with an NTBL have improved crystal quality, with a low threading dislocations density being yielded via the strain relaxation in the InGaN-based LEDs. Based on the results mentioned above, the electroluminescence results indicate that the light performance of InGaN-based LEDs with an NTBL can be enhanced by 45% and 42% at 20 mA and 100 mA, respectively. These results suggest that the strain relaxation and quality improvement in the GaN epilayer could be responsible for the enhancement of emission power. (C) 2015 Published by Elsevier B.V.
High performance 380-nm ultraviolet light-emitting-diodes with 3% efficiency droop by using free-standing GaN substrate manufacturing from GaAs substrate
(2014-07-07)
Shieh, Chen-Yu
;
Tsai, Ming-Ta
;
Li, Zhen-Yu
;
Kuo, Hao-Chung
;
Chang, Jeng-Yang
We investigated the influence of free-standing GaN (FS-GaN) substrates on the performance of ultraviolet light-emitting-diodes (UV-LEDs) grown on top by atmospheric pressure metal-organic chemical vapor deposition. High-resolution double-crystal x-ray diffraction (HRDCXD) analysis demonstrated high-order satellite peaks and clear fringes between them for UV-LEDs grown on the FS-GaN substrate, from which the interface roughness was estimated. In addition, the full width at half maximum of the HRDCXD rocking curve in the (0002) and the (1012) reflections were reduced to below 90 arc sec. The Raman results indicated that the GaN-based epilayer of strain free was grown. Additionally, the effect of the FS-GaN substrate on the crystal quality of the UV-LEDs was examined in detail by transmission electron microscopy (TEM). The TEM characterizations revealed no defects and V-pits were found in the scanned area. Based on the results mentioned above, the light output power of UV-LEDs on the FS-GaN substrate can be enhanced drastically by 80% and 90% at 20 and 100 mA, respectively. Furthermore, an ultralow efficiency degradation of about 3% can be obtained for the UV-LEDs on the FS-GaN substrate at a high injection current. The use of an FS-GaN substrate is suggested to be effective for improving the emission efficiency and droop of UV-LEDs grown thereon.