Enhanced photovoltaic performance of Y2O3:Ho3+/Yb3+ upconversion nanophosphor based DSSC and investigation of color tunability in Ho3+/Tm3+/Yb3+ tridoped Y2O3
(2020-04-25)
Tadge, Prachi
;
Yadav, Ram Sagar
;
Vishwakarma, Pradeep Kumar
;
Rai, S. B.
;
Chen, Teng-Ming
The present study reports the upconversion (UC) based color tuning in Y2O3:Ho3+/Yb3+, Y2O3:Tm3+/Yb3+ and Y2O3:Tm3+/Ho3+/Yb3+ phosphors synthesized through complex based precursor solution method. The Y2O3:Ho3+/Yb3+ phosphor emits intense green and weak red colors whereas the Y2O3:Tm3+/Yb3+ emits NIR and blue colors on excitation with 976 nm. The impact of the enhancement in the concentration of Yb3+ on the color point of codoped as well as tridoped phosphors has been studied in detail. When Y2O3:Tm3+/Ho3+/Yb3+ phosphor is excited by 976 nm laser, the phosphor emits dominant green color. This is due to energy transfer from Tm3+ to Ho3+ ions. The increase in the concentration of Yb3+ ion leads to a color tunability not only in the co-doped but also in the tridoped phosphors. Furthermore, we have incorporated Y2O3:Ho3+,Yb3+ UC phosphor into TiO2 electrode to form an UC based DSSC for converting near IR (NIR) light into visible where DSSCs typically have high sensitivity. The short-circuit current density (Jsc) as well as the open-circuit voltage (Voc) of the UC-TiO2 based cell was found to be 8.46% and 5.18% higher which in turn, resulted into a 10.33% enhancement in power conversion efficiency as compared to that of bare TiO2 based DSSC. Thus, the UC based Y2O3:Ho3+/Yb3+ may be useful in color tunability and DSSC applications. (C) 2019 Elsevier B.V. All rights reserved.
Structural and spectroscopic characterizations of a new near-UV-converting cyan-emitting RbBaScSi3O9:Eu2+ phosphor with robust thermal performance
(2017-08-05)
Ray, Sudeshna
;
Tadge, Prachi
;
Dhoble, S. J.
;
Nair, Govind B.
;
Singh, Akash
To facilitate the next generation of White Light Emitting Diodes (WLEDs) with higher color rendering and warm lighting, the development of inorganic phosphor for efficient conversion of photons from blue/near-UV light to other visible wavelengths is essential. In this regard, we demonstrate a systematic, cost effective, solution-processable, easily scalable and fully controllable synthesis of a series of RbBaScSi3O9:xEu(2+) (x = 0.2, 0.5, 2, 5, 7), a new cyan emitting scandium silicate based phosphor with 79% internal quantum efficiency under n-UV excitation with robust thermal performance. The concept as well as the methodology of using a "Mineral Inspired Approach" emerges as a new blueprint for the rational design of novel phosphor for phosphor converted WLEDs. The structural refinement, electronic structural calculation using "Density Functional Theory", characteristic photoluminescence study, lifetime measurement as well as the thermal quenching properties of the phosphor has been investigated in detail. Owing to the highly efficient cyan emission at lambda(max) similar to 492 nm a full-width at half-maximum of 63 cm(-1) that shows only very low thermal quenching (89.28% relative to the PL intensity at 150 degrees C with respect to that of measured at room temperature), reflects the great potential for the industrial application of this particular phosphor. (C) 2017 Elsevier B.V. All rights reserved.
Synthesis, luminescence and application of BaKYSi2O7:Eu2+ : A new blue-emitting phosphor for near-UV white-light LED
(2018-05-01)
Ray, Sudeshna
;
Tadge, Prachi
;
Dutta, Somrita
;
Chen, T. M.
;
Nair, Govind B.
A series of new silicate phosphors, Ba1-xEuxKYSi2O7 (BKY: Eu2+) (x = 0.005, 0.01, 0.02, 0.05, 0.07) have been synthesized from a water-soluble propylene glycol modified silane (PGMS) based silicon precursor by a solution approach. This phosphor can be efficiently excited by near-UV light and generates a broadband bright blue emission with internal Quantum Efficiency 34%. The detailed crystal structure of monoclinic BKY:Eu2+ was determined from the XRD profile using Rietveld refinement. Band gap was determined from Diffuse Reflectance Spectra using Kubelka Munk function. Steady state and time resolved Photoluminescence measurement as well as the thermal quenching properties of the phosphor have been investigated in detail. A highly efficient broadband blue emission centered lambda(max) similar to 460 nm with a full-width at half-maximum of 72 nm shows very low thermal quenching; 83.2% at 150 degrees C with respect to that measured at room temperature. Moreover, a white LED device has been fabricated by coating the as-synthesized phosphor with a standard red emitting CaAlSiN3:Eu2+ phosphor and a standard green emitting Ba2SiO4:Eu2+ phosphor. The LED device exhibited an excellent color-rendering index CRI of 84.0564 at a correlated color temperature of 3752.4 K with CIE color coordinates of (0.363, 0.293) under a 350 mA forward-bias current. The interesting excitation profile and robust thermal performance reflect the potential application of this phosphor for near UV- LED driven solid state lighting.