Degradation of Low Temperature Polycrystalline Silicon Thin Film Transistors under Negative Bias Temperature Instability Stress with Illumination Effect
(2010)
Lin, Chia-Sheng
;
Chen, Ying-Chung
;
Chang, Ting-Chang
;
Li, Hung-Wei
;
Hsu, Wei-Che
This work investigates negative bias temperature instability (NBTI) in low temperature polycrystalline silicon thin film transistors (LTPS TFTs) in a darkened and in an illuminated environment of different light intensities. Experimental results reveal that the generations of interface state density (N(it)) are identical under various illuminated intensity NBTI stresses. Nevertheless, the degradation of the grain boundary trap (N(trap)) under illumination was more significant than that for the darkened environment, with degradation increasing as illumination intensity increases. This phenomenon is mainly caused by the extra number of holes generated during the illuminated NBTI stress. The increased N(trap) degradation leads to an increase in the darkened environment leakage current. This indicates that more traps are generated in the drain junction region than from carrier tunneling via the trap, resulting in leakage current. Conversely, an increase in N(trap) degradation results in a decrease in the photoleakage current. This indicates that the number of recombination centers increases in the poly-Si bulk, affecting photosensitivity in LTPS TFTs.
Illumination-Assisted Negative Bias Temperature Instability Degradation in Low Temperature Polycrystalline Silicon Thin-Film Transistors
(2009)
Lin, Chia-Sheng
;
Chen, Ying-Chung
;
Chang, Ting-Chang
;
Hsu, Wei-Che
;
Chen, Shih-Ching
In this work, the negative bias temperature instability (NBTI) in low temperature polycrystalline silicon thin-film transistors in a darkened and in an illuminated environment was investigated. Experimental results reveal that the generation of interface state density (N(it)) showed no change between the different NBTI stresses. Nevertheless, the degradation of the grain boundary trap (N(trap)) under illumination was more significant than that in the darkened environment. This phenomenon is mainly caused by the extra number of holes generated during the illuminated NBTI stress.
Oxygen-Adsorption-Induced Anomalous Capacitance Degradation in Amorphous Indium-Gallium-Zinc-Oxide Thin-Film-Transistors under Hot-Carrier Stress
(2012)
Chung, Wan-Fang
;
Chang, Ting-Chang
;
Lin, Chia-Sheng
;
Tu, Kuan-Jen
;
Li, Hung-Wei
This paper investigates anomalous capacitance-voltage (C-V) degradation in amorphous indium-gallium-zinc-oxide (a-IGZO) thin-film-transistors (TFTs) under hot carrier stress. In vacuum hot carrier stress, both the gate-to-drain capacitance (C(GD)) and the gate-to-source capacitance (C(GS)) curves exhibited positive shifts due to electron trapping in the gate dielectric. In addition, an observed increase in capacitance value at a lower gate voltage in the C(GD) measurement only can be ascribed to interface state creation. However, when the hot carrier stress was performed in an oxygen-rich environment, the C(GD)-V(G) curve showed a significantly positive shift due to the electric-field-induced oxygen adsorption near the drain terminal. The degradation in the C(GS)-V(G) curve is due not only to the positive shift, but also the anomalous two step turn-on behavior. This phenomenon can be ascribed to the electron trapping in the gate dielectric and electric-field-induced oxygen adsorption on the channel layer, especially in the area adjacent to the drain terminal. The electron trapping increased the source energy barrier, with the electric-field-induced oxygen adsorption further raising the energy-band near the drain, resulting in a two-step turn-on behavior in the C(GS)-V(G) curve. (C) 2012 The Electrochemical Society. [DOI: 10.1149/2.075203jes] All rights reserved.