Browsing by Author "Wang, Chuan-Jyun"

Now showing 1 - 3 of 3

High throughput fabrication of large-area colloidal crystals via a two-stage electrophoretic deposition method
(2019-09-10)
Hung, Pei-Sung
;
Liao, Chen-Hong
;
Chou, Yu-Szu
;
Wang, Guang-Ren
;
Wang, Chuan-Jyun
An effective and high-throughput method is demonstrated to produce a colloidal crystal with impressive crystallinity. The fabrication procedure involves a two-stage electrophoresis process in which a vertical electrophoretic deposition of polystyrene microspheres (495 nm) is conducted on an ITO substrate to form a colloidal crystal in size of 4 x 4 cm(2), followed by a horizontal electrophoresis to improve the packing crystallinity. Relevant parameters associated with the horizontal electrophoresis step including voltage polarity, bipolar voltage offset, and operation frequency are investigated. Their effects over the crystallinity of the colloidal crystals are verified quantitatively and qualitatively by structural observation via scanning electron microscope and optical reflectance spectra. We determine that the imposition of an alternately-changing bias of 80/0/-120/0 V at 10 Hz (25 ms in each bias) enables the production of colloidal crystals with the largest grain size (106 mm) and the smallest grain boundary (170 nm), as compared to samples prepared from a single vertical electrophoresis step. We attribute the improved crystallinity of the colloidal crystal to the bipolar bias that engenders localized movements of the microspheres, rendering them to pack more closely with reduced defects. (C) 2019 Elsevier Ltd. All rights reserved.
Synthesis of IrO(2)decorated core-shell PS@PPyNH(2)microspheres for bio-interface application
(2020-09-11)
Hsieh, Tsung-Lin
;
Hung, Pei-Sung
;
Wang, Chuan-Jyun
;
Tso, Kuang-Chih
;
Wang, Han-Yi
In this paper, an effective approach is demonstrated for the fabrication of IrO2-decorated polystyrene@functionalized polypyrrole (core@shell; PS@PPyNH2) microspheres. The synthesis begins with the preparation of monodispersive PS microspheres with a diameter of 490 nm, by a process of emulsifier-free emulsion polymerization, followed by a copolymerization process involving pyrrole and PyNH(2)monomers in a PS microsphere aqueous suspension, to produce uniform PS@PPyNH(2)microspheres with a diameter of 536 nm. The loading of 2 nm IrO(2)nanoparticles onto the PS@PPyNH(2)microspheres can be easily adjusted by tuning the pH value of the IrO(2)colloidal solution and the PS@PPyNH(2)suspension. At pH 4, we successfully obtain IrO2-decorated PS@PPyNH(2)microspheres via electrostatic attraction and hydrogen bonding simultaneously between the negatively-charged IrO(2)nanoparticles and the positively-charged PS@PPyNH(2)microspheres. These IrO2-decorated PS@PPyNH(2)microspheres exhibit a characteristic cyclic voltammetric profile, similar to that of an IrO(2)thin film. The charge storage capacity is 5.19 mA cm(-2), a value almost five times greater than that of PS@PPyNH(2)microspheres. In addition, these IrO2-decorated PS@PPyNH(2)microspheres exhibit excellent cell viability and biocompatibility.
Synthesis of polystyrene@polypyrrole-COOH@Ag (core@shell@shell) microspheres for potential application in anisotropic conductive paste
(2020-03-15)
Wang, Chuan-Jyun
;
Hung, Pei-Sung
;
Chou, Shih-Cheng
;
Chung, Wei-An
;
Wu, Pu-Wei
We demonstrate a fabrication scheme for the synthesis of conductive core-shell (core@shell) nanoparticles consisting of polystyrene (PS) microspheres in size of 613 nm with consecutive coatings of functionalized polypyrrole (PPy-COOH) and Ag. The PPy-COOH precursors undergo polymerization on PS microspheres forming PS@PPy-COOH microspheres, followed by sensitization and Ag electroless deposition to produce PS@PPy-COOH@Ag microspheres in size of 717 nm. The PPy-COOH serves as the adhesive for intimate bonding of PS and Ag. Images from scanning and transmission electron microscopes confirm a Ag coating of 41-50 nm which is consisted of clustered nanoparticles forming a mono-layered film. From X-ray diffraction pattern, the Ag adopts a polycrystalline fcc structure with grain size of 12 nm. Results from thermal gravimetric analysis indicate a Ag loading of 54 wt%. By four-point-probe, the bulk conductivity for PS@PPy-COOH@Ag is 10,170 S m(-1). These microspheres show promising potential for anisotropic conductive paste. (C) 2019 Elsevier B.V. All rights reserved.