Investigation of the low-temperature AlGaN interlayer in AlGaN/GaN/AlGaN double heterostructure on Si substrate
(2014-11-01)
Hsiao, Yu-Lin
;
Wang, Yi-Jie
;
Chang, Chia-Ao
;
Weng, You-Chen
;
Chen, Yen-Yu
A low-temperature (LT) AlGaN interlayer is inserted in the Al0.1Ga0.9N back barrier layer of an Al0.2Ga0.8N/GaN/Al0.1Ga0.9N double heterostructure grown on a 150mm Si substrate. It is found that the 21-nm-thick LT-AlGaN interlayer plays an important role in stress relaxation and dislocation reduction of the Al0.1Ga0.9N back barrier layer, especially for screw dislocation reduction. In addition, a buffer breakdown voltage higher than 600V is achieved, which is much higher than those of conventional heterostructures. These results demonstrate the effectiveness of combining the LT-AlGaN interlayer and the Al0.2Ga0.8N/GaN/Al0.1Ga0.9N double heterostructure on a Si substrate to increase the breakdown voltage for high-power applications. (C) 2014 The Japan Society of Applied Physics
Material growth and device characterization of AlGaN/GaN single-heterostructure and AlGaN/GaN/AlGaN double-heterostructure field effect transistors on Si substrates
(2014-05-01)
Hsiao, Yu-Lin
;
Chang, Chia-Ao
;
Chang, Edward Yi
;
Maa, Jer-Shen
;
Chang, Chia-Ta
An Al0.2Ga0.8N/GaN/Al0.1Ga0.9N double-heterostructure field effect transistor (DH-FET) structure was grown on a 150-mm-diameter Si substrate and the crystalline quality of the epitaxial material was found to be comparable to that of an Al0.2Ga0.8N/GaN single-heterostructure field effect transistor (SH-FET) structure. The fabricated DH-FET shows a lower buffer leakage current of 9.2 x 10(-5) mA/mm and an improved off-state breakdown voltage of higher than 200V, whereas the SH-FET shows a much higher buffer leakage current of 6.0 x 10(-3) mA/mm and a lower breakdown voltage of 130 V. These significant improvements show that the Al0.2Ga0.8N/GaN/Al0.1Ga0.9N DH-FET is an effective structure for high-power electronic applications. (C) 2014 The Japan Society of Applied Physics