High-operation-temperature Aluminum-based SPP Nanolasers
(2016)
Chou, Yu-Hsun
;
Hong, Kuo-Bin
;
Chou, Bo-Tsun
;
Wu, Yen-Mo
;
Shih, Jheng-Hong
Metal-insulator-semiconductor structures has widely adopted in plasmonics lasers. However, we found that the insulator is not necessary if permittivity combination of laser structures is properly designed. Single-mode laser operation was demonstrate in devices without artificial insulator layers. Moreover, the operation temperature can achieve to 353 K.
High-Operation-Temperature Plasmonic Nanolasers on Single-Crystalline Aluminum
(2016-05)
Chou, Yu-Hsun
;
Wu, Yen-Mo
;
Hong, Kuo-Bin
;
Chou, Bo-Tsun
;
Shih, Jheng-Hong
The recent development of plasmonics has overcome the optical diffraction limit and fostered the development of several important components including nanolasers, low-operation-power modulators, and high-speed detectors. In particular, the advent of surface-plasmon-polariton (SPP) nanolasers has enabled the development of coherent emitters approaching the nanoscale. SPP nanolasers widely adopted metal insulator semiconductor structures because the presence of an insulator can prevent large metal loss. However, the insulator is not necessary if permittivity combination of laser structures is properly designed. Here, we experimentally demonstrate a SPP nanolaser with a ZnO nanowire on the as-grown single-crystalline aluminum. The average lasing threshold of this simple structure is 20 MW/cm(2), which is four-times lower than that of structures with additional insulator layers. Furthermore, single-mode laser operation can be sustained at temperatures up to 353 K. Our study represents a major step toward the practical realization of SPP nanolasers.
Realization of UV Plasmonic Nanolasers With Extremely Small Mode Volume
(2015-11-01)
Chou, Bo-Tsun
;
Chou, Yu-Hsun
;
Chiang, Chih-Kai
;
Wu, Yen-Mo
;
Lin, Tzy-Rong
It is difficult to operate plasmonic nanolasers on silver films in the ultraviolet regime owing to the bending-back effect of surface plasmon dispersion. In this paper, we report on plasmonic lasers comprised of a ZnO nanowire lying on a single-crystalline silver film with a SiO2 spacer layer. The silver can strongly shrink the mode volume, thereby boosting the Purcell factor. Meanwhile, the SiO2 spacer thickness is optimized to adjust the surface plasmon dispersion curve so that the lasing wavelength can be located at a large dispersion region, thereby achieving a large group index of 55, an ultra-small effective mode volume of 3.5 x 10(-3)lambda(3), and low-threshold of 11 MW/cm(2).
Single-crystalline aluminum film for ultraviolet plasmonic nanolasers
(2016-01-27)
Chou, Bo-Tsun
;
Chou, Yu-Hsun
;
Wu, Yen-Mo
;
Chung, Yi-Cheng
;
Hsueh, Wei-Jen
Significant advances have been made in the development of plasmonic devices in the past decade. Plasmonic nanolasers, which display interesting properties, have come to play an important role in biomedicine, chemical sensors, information technology, and optical integrated circuits. However, nanoscale plasmonic devices, particularly those operating in the ultraviolet regime, are extremely sensitive to the metal and interface quality. Thus, these factors have a significant bearing on the development of ultraviolet plasmonic devices. Here, by addressing these material-related issues, we demonstrate a low-threshold, high-characteristic-temperature metal-oxide-semiconductor ZnO nanolaser that operates at room temperature. The template for the ZnO nanowires consists of a flat single-crystalline Al film grown by molecular beam epitaxy and an ultrasmooth Al2O3 spacer layer synthesized by atomic layer deposition. By effectively reducing the surface plasmon scattering and metal intrinsic absorption losses, the high-quality metal film and the sharp interfaces formed between the layers boost the device performance. This work should pave the way for the use of ultraviolet plasmonic nanolasers and related devices in a wider range of applications.