Broadband Omnidirectional Light Trapping in Gold-Decorated ZnO Nanopillar Arrays
(2017-04-05)
Chang, Yuan-Ming
;
Lin, Man-Ling
;
Lai, Tung-Yen
;
Chen, Chang-Hung
;
Lee, Hsin-Yi
The photoluminescence (PL) and reflectivity characteristics of zinc oxide nanopillars- (ZnO-NPs) grown on indium tin oxide (ITO)-coated glasses were investigated. The room temperature PL showed bright -white -light emission for the undoped ZnO-NPs grown at 600 degrees C, suggesting the close relation between the optical characteristic and "the growth conditions being, carried out for,obtaining the present ZnO-NPs. The reflectivity of the as -grown ZnO-NPs array was about, similar to 29% with the wavelength of the incident light ranging from 200 to 1800 nm. Nevertheless, the reflectance reduced significantly to less than 9.9% when a layer of gold (Au) was deposited on ZnO=NPg by sputtering for 5 min, corresponding to more than 65% reduction in Au -coated ZnQ-NPs (Au/ZnO-NPs). Moreover, the angle -resolved reflectance measurement's on the present Au/ZnO-NPs array show an omnidirectional light -trapping characteristic. These remarkable characteristics, broadband and omnidirectional light -trapping -of Ati/ZnO-NPs, are attributed to the extended effective optical path of the incident light due to subwavelength scattering resulting,from the presence of Au nanoparticics.
Field Emission Properties of Gold Nanoparticle-Decorated ZnO Nanopillars
(2012-12-01)
Chang, Yuan-Ming
;
Lin, Man-Ling
;
Lai, Tung-Yen
;
Lee, Hsin-Yi
;
Lin, Chih-Ming
The structural and optoelectronic properties of ZnO nanopillars (ZnO-NPs) grown on Si substrates by the vapor transport deposition method were investigated. In particular, by varying the deposition duration and hence the morphology of the vertically aligned ZnO-NPs, the resultant field emission characteristics were systematically compared. In addition to identifying the advantageous field emission properties exhibited in the pencil-like ZnO-NPs, we observed that by adhering Au nanoparticles on the surface of the ZnO-NPs the turn-on field and the maximum current density can be drastically improved from 3.15 V/mu m and 0.44 mA/cm(2) at 5 V/mu m for the best ZnO-NPs to 2.65 V/mu m and 2.11 mA/cm(2) at 5 V/mu m for Au/ZnO-NPs, respectively. The enhancement of field emission characteristics that resulted from Au-nanoparticle decoration is discussed on the basis of charge-transfer-induced band structure modifications.
Improvement of Epitaxy GaN Quality Using Liquid-Phase Deposited Nano-Patterned Sapphire Substrates
(2012-12-15)
Hsieh, Cheng-Yu
;
Lin, Bo-Wen
;
Cho, Hsin-Ju
;
Wang, Bau-Ming
;
Chang, Nancy
A relatively simple and easy and inexpensive liquid-phase deposition (LPD) method is employed to introduce nanoscale silica hemispheres on sapphire substrates for fabricating a nano-patterned sapphire substrate (NPSS). Compared with GaN grown on sapphire without any pattern, the NPSS-GaN film is of much better quality as observed by scanning electron microscopy, transmission electron-microscopy, X-ray diffraction, cathodoluminescence, and photoluminescence. This is because GaN is initiated from the c-plane instead of the LPD-silica surface. In addition, many dislocations within the NPSS-GaN bend toward the patterns, or end at the GaN/void interfaces.