Capabilities of time-resolved X-ray excited optical luminescence of the Taiwan Photon Source 23A X-ray nanoprobe beamline
(2020-01-01)
Lin, Bi-Hsuan
;
Wu, Yu-Hao
;
Li, Xiao-Yun
;
Hsu, Hsu-Cheng
;
Chiu, Yu-Cheng
Time-resolved X-ray excited optical luminescence (TR-XEOL) was developed successfully for the 23A X-ray nanoprobe beamline located at the Taiwan Photon Source (TPS). The advantages of the TR-XEOL facility include (i) a nano-focused X-ray beam (<60 nm) with excellent spatial resolution and (ii) a streak camera that can simultaneously record the XEOL spectrum and decay time. Three time spans, including normal (30 ps to 2 ns), hybrid (30 ps to 310 ns) and single (30 ps to 1.72 mu s) bunch modes, are available at the TPS, which can fulfil different experimental conditions involving samples with various lifetimes. It is anticipated that TR-XEOL at the TPS X-ray nanoprobe could provide great characterization capabilities for investigating the dynamics of photonic materials.
Hard X-ray nanoprobe and time-resolved XEOL to observe increasing luminescence of ZnO and GaN epitaxial structures
(2019-10-21)
Lin, Bi-Hsuan
;
Wu, Yu-Hao
;
Wu, Tai-Sing
;
Wu, Yung-Chi
;
Li, Xiao-Yun
Hard X-ray excited optical luminescence (XEOL) with a nanofocused beam provides both excellent spatial resolution and high enough peak power density, which makes XEOL mapping and luminescence dynamics study achievable. We present here the time and X-ray intensity dependence of the near-band-edge (NBE) luminescence from the nonpolar a-plane MgZnO/ZnO multiple quantum wells (MQWs): the emission intensity increases more than 10 times after high X-ray irradiation. Different from the well-known NBE emission lifetime of ZnO (less than 1 ns), the long decay time gradually decreases from 130 ns to 35 ns with the increasing X-ray irradiation time. We attribute the observed changes in NBE luminescence to the excitation of the Mg-related energy state by the high energy X-ray nanobeam. This suggestion was further confirmed in the XEOL spectra of the Mg-doped and Si-doped c-plane GaN epi-films. Published under license by AIP Publishing.
Observation of anomalous emissions of nonpolar a-plane MgZnO and ZnO epi-films based on XEOL and time-resolved XEOL in hybrid bunch mode
(2020-08-01)
Lin, Bi-Hsuan
;
Wu, Yu-Hao
;
Wu, Yung-Chi
;
Liu, Wei-Rein
;
Lee, Chien-Yu
X-ray excited optical luminescence (XEOL) using an x-ray nanobeam operating in the hybrid bunch mode provides not only a sufficiently high peak power density but also high-quality temporal domain measurements for studying the luminescence dynamics of photonic materials and devices. We used these features to investigate the peculiar emission behavior of the as-grown and rapid thermal annealing (RTA)-treated a-plane MgZnO epi-films, from which an anomalous emission was observed at similar to 325 nm, along with a rapid increase in near-band edge (NBE) emission with increasing x-ray irradiation time. This peculiar emission behavior was also observed in the cathodoluminescence spectra obtained under electron beam excitation. Increases in the NBE emission intensity of the RTA-treated a-plane MgZnO epi-film were observed in terms of both photoluminescence and small anomalous emissions of XEOL. This can be explained by the effective transfer of Mg atoms from interstitial sites to suitable sites as a result of RTA treatment. Based on comparison with an a-plane ZnO epi-film without Mg, we conclude that the anomalous emission peak is caused by Mg-related energy states created by the high-dose x-ray or electron beam irradiation. Furthermore, the rapid increase in NBE emission and the reduction in the long decay lifetime can be attributed to charge transfer from the Mg clusters, which are thus responsible for the anomalous emissions.