Effect of thermal annealing for W/beta-Ga2O3 Schottky diodes up to 600 degrees C
(2019-11-01)
Xian, Minghan
;
Fares, Chaker
;
Ren, Fan
;
Gila, Brent P.
;
Chen, Yen-Ting
The electrical and structural properties of sputter-deposited W Schottky contacts with Au overlayers on n-type Ga2O3 are found to be basically stable up to 500 degrees C. The reverse leakage in diode structures increases markedly (factor of 2) for higher temperature annealing of 550-600 degrees C. The sputter deposition process introduces near-surface damage that reduces the Schottky barrier height in the as-deposited state (0.71 eV), but this increases to 0.81 eV after a 60 s anneal at 500 degrees C. This is significantly lower than conventional Ni/Au (1.07 eV), but W is much more thermally stable, as evidenced by Auger electron spectroscopy of the contact and interfacial region and the minimal change in contact morphology. The contacts are used to demonstrate 1.2 A switching of forward current to -300 V reverse bias with a reverse recovery time of 100 ns and a dI/dt value of 2.14 A/mu s. The on/off current ratios were >= 10(6) at -100V reverse bias, and the power figure-of-merit was 14.4 MW cm(-2). Published by the AVS.