Effect of activating flux and welding parameters on performance of aluminum alloy weldment in GTA welding
(2012)
Lin, Hsuan-Liang
;
Juang, Hung-Wei
;
Yan, Jia-Ching
;
機械工程學系
;
Department of Mechanical Engineering
The purpose of this work was to investigate the effect of activating fluxes and welding parameter to the penetration and depth-to-width ratio (DWR) of 6061 aluminum alloy welds. Bead-on-plate argon gas tungsten arc (GTA) welding process was made on 6061 aluminum alloy of plate without filling metals. The activating fluxes used in the experiment were CaO, ZnO, SiO2, TiO2, Al2O3, Cr2O3, CaF2 and Na2CO3. Based on the higher penetration of weld bead and welding arc voltage, four fluxes were selected to create three new mixtures using 50% of each original fluxes. The mixed fluxes were used to investigate the effect to the welding penetration. Finally, The Taguchi method was employed to achieve optimal DWR of weld bead and investigate the welding parameters that significantly affect welding quality. The experimental procedure of GTA welding with activating flux via the Taguchi method produced full penetration of weld bead on a 6.35 mm thickness of 6061 aluminum alloy plate with single pass weld.
Optimization of weld bead geometry in the activated GMA welding process via a grey-based Taguchi method
(2014-08-01)
Lin, Hsuan-Liang
;
Yan, Jia-Ching
;
機械工程學系
;
Department of Mechanical Engineering
We optimized the weld bead geometry of 6061 aluminum alloy welds pre-coated with activating flux before gas metal arc (GMA) welding. In this activated GMA welding process, there were five single component fluxes used in the initial experiment to evaluate the penetration capability of bead-on-plate GMA welds. Based on the higher penetration of weld bead, two single component fluxes were selected to create mixed component flux in next stage. The grey-based Taguchi method was employed to obtain the optimal welding parameters that were considered with multiple quality characteristics such as penetration, depth-to-width ratio (DWR) and fusion area of GMA welds. The experimental procedure of the proposed approach not only increases penetration of 6061 aluminum alloy welds, but also improves the DWR and fusion area of GMA butt-joint welds simultaneously.
Optimization of weld bead geometry in the activated GMA welding process via a grey-based Taguchi method
(2014-08-01)
Lin, Hsuan-Liang
;
Yan, Jia-Ching
;
機械工程學系
;
Department of Mechanical Engineering
We optimized the weld bead geometry of 6061 aluminum alloy welds pre-coated with activating flux before gas metal arc (GMA) welding. In this activated GMA welding process, there were five single component fluxes used in the initial experiment to evaluate the penetration capability of bead-on-plate GMA welds. Based on the higher penetration of weld bead, two single component fluxes were selected to create mixed component flux in next stage. The grey-based Taguchi method was employed to obtain the optimal welding parameters that were considered with multiple quality characteristics such as penetration, depth-to-width ratio (DWR) and fusion area of GMA welds. The experimental procedure of the proposed approach not only increases penetration of 6061 aluminum alloy welds, but also improves the DWR and fusion area of GMA butt-joint welds simultaneously.