Design of novel TiO2-SiO2 core-shell helical nanostructured anti-reflective coatings on Cu(In,Ga)Se-2 solar cells with enhanced power conversion efficiency
(2019-05-14)
Chen, Chia-Wei
;
Tsai, Hung-Wei
;
Wang, Yi-Chung
;
Su, Teng-Yu
;
Yang, Chen-Hua
Introducing an anti-reflective coating (ARC) is the last step of fabricating Cu(In,Ga)Se-2 solar cells with enhanced photo-generated current by reducing the reflectance of visible light. The use of nanostructures in ARC has been intensively investigated because this can prolong the optical path length by a scattering effect or by the formation of a refractive index gradient. Herein, we proposed the use of TiO2 helical nanostructures using glancing angle deposition (GLAD), and then synthesized SiO2 surrounding the helical nanostructures to further decrease the reflectance by producing a refractive index gradient. The optimized values of TiO2 and SiO2 thicknesses are 150 nm and 3 nm determined by the finite-difference time-domain (FDTD) simulation on Cu(In,Ga)Se-2 solar cells. The suppression of reflectance led to enhanced light absorption across a broad wavelength range, and boosted the J(SC) from 20.66 to 22.51 mA cm(-2), resulting in improved power conversion efficiency (PCE) from 6.32 to 7.00% after applying the TiO2-SiO2 core-shell nanostructures as the ARC. This 10.75% PCE enhancement suggests that the novel TiO2-SiO2 core-shell nanostructures have great potential as ARC for Cu(In,Ga)Se-2 solar cells, and it would be beneficial for development in the photovoltaic field in both research and applications.
Phase-Engineered Type-II Multimetal-Selenide Heterostructures toward Low-Power Consumption, Flexible, Transparent, and Wide-Spectrum Photoresponse Photodetectors
(2018-05-29)
Chen, Yu-Ze
;
Wang, Sheng-Wen
;
Su, Teng-Yu
;
Lee, Shao-Hsin
;
Chen, Chia-Wei
Phase-engineered type-II metal-selenide heterostructures are demonstrated by directly selenizing indium-tin oxide to form multimetal selenides in a single step. The utilization of a plasma system to assist the selenization facilitates a low-temperature process, which results in large-area films with high uniformity. Compared to single-metal-selenide-based photodetectors, the multimetal-selenide photodetectors exhibit obviously improved performance, which can be attributed to the Schottky contact at the interface for tuning the carrier transport, as well as the type-II heterostructure that is beneficial for the separation of the electron-hole pairs. The multimetal-selenide photodetectors exhibit a response to light over a broad spectrum from UV to visible light with a high responsivity of 0.8 A W-1 and an on/off current ratio of up to 10(2). Interestingly, all-transparent photodetectors are successfully produced in this work. Moreover, the possibility of fabricating devices on flexible substrates is also demonstrated with sustainable performance, high strain tolerance, and high durability during bending tests.