Fabricating 43-mu m-Thick and 12% Efficient Heterojunction Silicon Solar Cells by Using Kerfless Si(111) Substrates
(2015-01-01)
Du, Chen-Hsun
;
Chen, Chien-Hsun
;
Wang, Teng-Yu
;
Hsiao, Jui-Chung
;
Yeh, Chun-Ming
A 43-mu m-thick Si(111) substrate was obtained using the stress-induced lift-off method with a screen-printed metal paste layer as the stress-generation layer. The reflection of the metal-removed side of the Si(111) substrate was lower than that of the exfoliated side because of high surface roughness resulting from the reaction between the metal paste and the silicon substrate at 700 degrees C. After aggressive etching with an alkaline solution for the peeled silicon substrate, the efficiency of the heterojunction silicon solar cell was improved from 0.87% to 12%. (C) The Author(s) 2015. Published by ECS. All rights reserved.
Organic thin-film transistors with AIN film as a gate-insulator by RFIICP sputtering
(2005-01-01)
Yen, Kuo-Hsi
;
Zan, Hsiao-Wen
;
Ko, Chueh-Ping
;
Liu, Pu-Kuan
;
Chang, Tzu-Yueh
We firstly fabricated the organic thin-film transistors with sputtered-AlN film as the gate insulator. The AlN film was deposited by the RF-ICP (Induced Couple Plasma) sputtering. The demonstrated pentacene based TFTs had on/off current ratio around 4 and mobility around 5x10(-4) cm(2)/Vs without any surface treatment and pentacene purification. All optimized conditions for this new proposed device were under processing.