Fabricating 43-mu m-Thick and 12% Efficient Heterojunction Silicon Solar Cells by Using Kerfless Si(111) Substrates
(2015-01-01)
Du, Chen-Hsun
;
Chen, Chien-Hsun
;
Wang, Teng-Yu
;
Hsiao, Jui-Chung
;
Yeh, Chun-Ming
A 43-mu m-thick Si(111) substrate was obtained using the stress-induced lift-off method with a screen-printed metal paste layer as the stress-generation layer. The reflection of the metal-removed side of the Si(111) substrate was lower than that of the exfoliated side because of high surface roughness resulting from the reaction between the metal paste and the silicon substrate at 700 degrees C. After aggressive etching with an alkaline solution for the peeled silicon substrate, the efficiency of the heterojunction silicon solar cell was improved from 0.87% to 12%. (C) The Author(s) 2015. Published by ECS. All rights reserved.
Functionalization, re-functionalization and rejuvenation of ssDNA nanotemplates
(2012)
Lin, Ming-Yu
;
Ho, Fu Han
;
Yang, Chung-Yao
;
Yeh, J. Andrew
;
Yang, Yuh-Shyong
Single-stranded DNA (ssDNA) with repetitive sequence was demonstrated to be a versatile nanotemplate for introducing biological activity in a self-assembled manner. Re-functionalization and rejuvenation of the ssDNA nanotemplate were achieved under mild biological conditions without using high temperature and strong alkaline treatment to denature DNA.