Browsing by Author "Yen, Cheng-Yo"

Now showing 1 - 3 of 3

Mechanical properties of the hexagonal HoMnO(3) thin films by nanoindentation
(2010-10-22)
Yen, Cheng-Yo
;
Jian, Sheng-Rui
;
Lai, Yi-Shao
;
Yang, Ping-Feng
;
Liao, Ying-Yen
The structural and nanomechanical characteristics of the hexagonal HoMnO(3) (HMO) thin films are investigated by means of X-ray diffraction (XRD), atomic force microscopy (AFM) and nanoindentation techniques in this study. The HMO thin films were deposited on YSZ(1 1 1) substrates by pulsed laser deposition (PLD). The XRD results reveal only pure (0 0 0 1)-oriented hexagonal HMO reflections without any discernible traces of impurity or secondary phases. Nanoindentation results exhibit discontinuities in the load-displacement curve (so-called multiple "pop-ins" event) during loading, indicating possible involvement of dislocation activities. No discontinuities were observed on unloading segment of the load-displacement curve. Continuous stiffness measurements (CSM) technique was carried out in the nanoindentation tests to determine the hardness and Young's modulus of the hexagonal HMO thin films. The obtained hardness and Young's modulus of the hexagonal HMO thin films are 14.2 +/- 0.7 GPa and 219.2 +/- 10.6 GPa, respectively with the room-temperature fracture toughness being in the order of 0.4 +/- 0.2 MPa m(1/2). (c) 2010 Elsevier B.V. All rights reserved.
Mechanical properties of the hexagonal HoMnO3 thin films by nanoindentation
(2010-10-22)
Yen, Cheng-Yo
;
Jian, Sheng-Rui
;
Lai, Yi-Shao
;
Yang, Ping-Feng
;
Liao, Ying-Yen
The structural and nanomechanical characteristics of the hexagonal HoMnO3 (HMO) thin films are investigated by means of X-ray diffraction (XRD), atomic force microscopy (AFM) and nanoindentation techniques in this study. The HMO thin films were deposited on YSZ(1 1 1) substrates by pulsed laser deposition (PLD). The XRD results reveal only pure (0 0 0 1)-oriented hexagonal HMO reflections without any discernible traces of impurity or secondary phases. Nanoindentation results exhibit discontinuities in the load-displacement curve (so-called multiple "pop-ins" event) during loading, indicating possible involvement of dislocation activities. No discontinuities were observed on unloading segment of the load-displacement curve. Continuous stiffness measurements (CSM) technique was carried out in the nanoindentation tests to determine the hardness and Young's modulus of the hexagonal HMO thin films. The obtained hardness and Young's modulus of the hexagonal HMO thin films are 14.2 +/- 0.7 GPa and 219.2 +/- 10.6 GPa, respectively with the room-temperature fracture toughness being in the order of 0.4 +/- 0.2 MPa m(1/2). (c) 2010 Elsevier B.V. All rights reserved.
The deformation behavior and fracture toughness of single crystal YSZ(111) by indentation
(2018-02-25)
Yen, Cheng-Yo
;
Jian, Sheng-Rui
;
Tseng, Yu-Chin
;
Juang, Jenh-Yih
;
電子物理學系
The nano-scale deformation behaviors and indentation-induced fracture features of the (111)-oriented yttrium-stabilized zirconia single crystal (YSZ(111)) were investigated by Berkovich and micro-Vicker indentations, respectively. The load-displacement curves in the Berkovich nano-indentation experiments evidently exhibited indentation-induced single "pop-in" phenomenon during loading, indicating that the nano-scale deformation in the YSZ(111) crystals is due primarily to the activities of dislocation nucleation and propagation. Based on this scenario, the number of nanoindentation-induced dislocation loops giving rise to the pop-in event was estimated to be around 2 x 10(5) with a critical radius of similar to 2 nm. The hardness and Young's modulus of YSZ(111) single crystal obtained by the continuous contact stiffness measurements (CSM) mode were 22.3 +/- 1.1 GPa and 270.6 +/- 8.5 GPa, consistent with those reported previously in the literature. In addition, the fracture toughness of YSZ(111) single crystal was estimated to be about 1.4-1.6 MPa m(1/2). (C) 2017 Elsevier B.V. All rights reserved.